纳米晶体
1.
Line-shape analysis of electroabsorption spectrum of CdS_(0.1)Se_(0.9) nanocrystals;
CdS_(0.1)Se_(0.9)纳米晶体共振电吸收谱的线形分析
2.
Synthesis of Nitrogen-Doped Fullercnes, Carbon Nanotubes and Nanocrystals in Nitrogen Atmosphere;
氮气氛中合成杂氮球烯、碳纳米管及纳米晶体的研究
3.
Molecular Dynamics Simulation for Atomic Structure and Properties of Nanocrystal of Silver;
分子动力学模拟纳米晶体银的结构和性能
2)  nanocrystalline
纳米晶体
1.
Study on preparation and structural characteristics of ZnFe_2O_4 nanocrystalline;
铁酸锌纳米晶体的制备及表面光伏特性研究
2.
Electrodeposition of nanocrystalline Fe-Ni-Cr alloy foil in trivalent chromium bath;
三价铬镀液中电沉积纳米晶体Fe-Ni-Cr合金箔
3.
Synthesis of nanocrystalline nickel by direct current electrodeposition;
直流电沉积法制备纳米晶体
3)  nanocrystals
纳米晶体
1.
Fabrication and properties of ZnO nanocrystals by laser irradiation under coaxially transporting O_2;
ZnO纳米晶体的同轴送氧激光制备及其特性
2.
The growth and characteristics of CdSeS nanocrystals in glass;
玻璃中CdSeS纳米晶体的生长及其性能
3.
Research on low-temperature heat capacity and thermal stabilit of SnO_2 and ZnO nanocrystals;
纳米晶体SnO_2、ZnO的低温热容及热稳定性研究
4)  nano-crystalline
纳米晶体
1.
Study on mechanochemistry synthesis for nano-crystalline;
机械力化学合成纳米晶体的研究
2.
The synthesizing process and mechanism of nano-crystalline BaTiO3 by mechanochemistry that ground the mixture powder of BaO and anatase TiO2 was studied by XRD, TEM and HR- TEM.
晶体形成经过成核和生长两个阶段,但生长到一定程度时达到动态平衡,合成的BaTiO3纳米晶体颗粒尺寸为10~30 nm。
3.
The nano-crystalline BaTiO3 was successfully synthesized by grinding the mixture of BaO and anatase TiO2 in a high-energy mill in nitrogen atmosphere and its mechanism was also discussed.
发现在一定操作参数条件下,粉磨初期为无定形形成期(15h以前),混合物颗粒粒度减小,晶格畸变,转变为无定形;粉磨中期为固相反应期(15~30h);BaO与TiO2在机械力的作用下产生固相反应生成BaTiO3,同时BaTiO3晶粒长大;粉磨后期又转入动态平衡期(30h以后),固相反应基本结束,已生成的BaTiO3的晶粒生长与粉磨引起的晶粒减小处于动态平衡;XRD,SEM;TEM研究表明:合成BaTiO3纳米晶体的晶粒尺寸为10~30nm。
5)  nano crystalline
纳米晶体
1.
This paper introduces the development,structure and the principle of high efficiency dye nano crystalline solar cells,and put for ward some key problems to solve.
本文介绍了高效染料纳米晶体太阳能电池的发展、结构和工作原理 ,并在此基础上提出一些今后需要解决的问题。
6)  nanopowder
纳米晶粉体
1.
BaTiO_3 nanopowder was successfully synthesized from alkoxide solution precursor by solgel process.
采用金属钡与乙二醇甲醚反应,形成乙二醇甲氧钡,再与钛酸四丁酯按照钡钛比为1∶1的摩尔比配料混合后在130℃回流1h,获得钡钛复合醇盐,然后加入一定量的去离子水,溶液迅速成胶,将湿凝胶陈化—干燥—热处理,成功合成了钛酸钡纳米晶粉体,合成温度低于150℃;且不同的加水量不仅影响凝胶的外观,同样对凝胶的析晶温度和晶体的种类有着重要的影响,当水与溶胶中钡离子的摩尔比为xw≥3时,均可得到纯净的钛酸钡纳米晶粉体。
补充资料:铁酸锌纳米晶体材料
分子式: ZnFe2O4 
CAS号:

性质:具有纳米尺度的晶体材料。不同熔烧温度(300~700℃),可得不同粒径(10~60nm)的铁酸锌材料。采用硫酸亚铁和硫酸锌混合,制得碱式碳酸盐前驱体,然后直接焙烧制备出铁酸锌纳米晶体材料。铁酸锌是性能优良的软磁材料、丁烯氧化脱氢的催化剂,具有很高的光催化活性及对可见光敏感的半导体催化剂。铁酸锌纳米晶体粒子是性能优良的透明无机颜料。

说明:补充资料仅用于学习参考,请勿用于其它任何用途。