1) non-equilibrium grain-boundary segregation
非平衡晶界偏聚
1.
The dynamic curve of non-equilibrium grain-boundary segregation and the impact temperature curve for 2.
25Cr1Mo和12Cr1MoV钢式样的非平衡晶界偏聚动力学曲线以及冲击温度曲线。
2) non-equilibrium segregation
非平衡晶界偏聚
1.
By solution treatment,isothermal aging treatmenmt and impact test, the critical time t_(c) for non-equilibrium segregation of residual element Tin in 0.
通过固溶处理和等温时效处理及冲击试验等简单方法,确定出连续冷却过程中残留元素Sn在低碳钢中发生的非平衡晶界偏聚及在不同温度下的临界时间tc。
3) non-equilibrium grain boundary segregation
非平衡晶界偏聚
1.
The non-equilibrium grain boundary segregation of boron in Ni_3Al-B alloys was determined by Auger electron spectroscopy(AES) in conjunction with ion sputtering in a cooling rate range 0.
９１Ｋ／ｓ的冷速范围内，用俄歇剖层分析确定了含硼Ｎｉ_３Ａｌ合金中硼的非平衡晶界偏聚行为。
4) equilibrium grain boundary segregation
平衡晶界偏聚
1.
Study on mechanism of temper embrittlement for step-cooling test based on the theory of equilibrium grain boundary segregation;
基于平衡晶界偏聚理论的步冷试验脆化机理研究
2.
Study on further embrittlement mechanism in 2.25Cr-1Mo steel based on theory of equilibrium grain boundary segregation
2.25Gr-1Mo钢基于平衡晶界偏聚理论的连续脆化机理研究
3.
According to the theory of the equilibrium grain boundary segregation it s concluded that the lower .
据平衡晶界偏聚理论,说明时效温度越低,磷的平衡偏聚量越大,而对应试样的韧脆转变温度越高,断裂形态由解理方式转变为沿晶方式。
5) non-equilibrium grain-boundary
非平衡晶界
1.
Based on the non-equilibrium grain-boundary cosegregation(NGCS) model,the cosegregation kinetics of Cr and N in NiCrMoV steel in the temperature range of 700-900 K is analyzed.
在非平衡晶界共偏聚理论基础上,分析了NiCrMoV钢中铬和氮在700~900 K下的共偏聚动力学。
6) Non-Equilibrium Segregation
非平衡偏聚
1.
The non-equilibrium segregation of boron on grain boundaries experienced three stages when the samples were cooled from 1150℃ to 640℃ at 2 ℃ /s, and transformed to boron precipitates at 860℃ .
采用硼（Ｂ）径迹照相法和透射电镜从实验上观察了连续冷却过程中Ｂ在晶界非平衡偏聚的发生发展过程。
2.
Grain boundary non-equilibrium segregation phenomenon has been found in many alloysystems.
溶质晶界非平衡偏聚现象已在大量合金系中发现。
3.
This phenomenon could only be explained by diffusion of vacancy-Si complex inducing non-equilibrium segregation.
这种偏聚只能用空位-Si原子复合体扩散导致的非平衡偏聚理论来解释。
补充资料：非晶金属
| 非晶金属 amorphous metal 原子排列在三维空间无长程有序的金属。因其具有类似玻璃的某些结构特征，故又称金属玻璃。非晶金属通常采用熔体急冷法制备。其制备过程是：向一高速运动的、导热性好的金属辊面上喷一薄层合金熔体，熔体因急冷而来不及成核结晶，从而形成非晶金属带。此外，还可采用原子蒸发、机械合金化、表面激光处理非晶化等方法制备非晶金属。 与晶态金属相比，非晶金属是一种特殊的物质状态，其微观结构特征决定了它具有许多优异性能，如优异的软磁性能、力学性能、耐腐蚀性能、催化性能、电学性能及对中子射线和γ射线的耐辐照性能等。研究最多、应用最广的非晶金属是非晶态软磁合金，有铁基、钴基、铁镍基和铁钴镍基等合金。铁基非晶合金如铁硅合金，具有高饱和磁通密度、低铁损、低密度和价廉等优点，是制造航空变压器较理想的铁芯材料；铁硅硼合金具有高电阻和极低铁损，容易形成低剩磁状态，其脉冲磁特性明显优于晶状硅钢和玻莫合金，是制造脉冲变压器的铁芯材料。铁基非晶合金还具有很高的磁致伸缩效应和高的电阻率，其非晶条带有利于制成快速响应的传感器，因此是一种新型传感器材料。钴基非晶合金的磁通密度和磁导率高，热稳定性好，同时还具有较高的耐磨性和耐蚀性，是一种性能优良的磁头材料。由于其没有晶界，所以用其制成的磁头可避免尖部脱落，磁头与磁带的摩擦噪音也比一般磁头小，音响效果好，且使用寿命长。 |