1) spheroidizing annealing
球化退火
1.
In order to solve the problem of crack deformation tendency of the quenched steel wires for a uniform structure,development is done to the special wire of hi-carbon and low alloy,finding that there is variation of spheroidizing annealing processed structure under the same spheroidizing annealing process once drawed.
为了改善针布齿条淬火时的变形开裂倾向性,使其最终性能均匀,研究了针布齿条专用高碳低合金钢丝经过不同程度拉拔变形后,在相同球化退火工艺下具有差异的球化退火组织,并且比较了经较大拉拔变形后钢丝退火前后的组织差异,以及该钢丝经轧制前后的组织变化情况。
2.
The carbide morphology and distribution in the microstructure of 4Cr10Si2Mo steel have been improved through the improvement of spheroidizing annealing proce.
通过改进球化退火工艺,使4Cr10Si2Mo钢的显微组织中的碳化物形态、分布得到改善,气门电镦的质量有了明显的提高。
3.
The effects of rolling process on spheroidizing annealing of GCr15 were studied by thermo-simulation.
通过热模拟的方法研究轧制工艺对GCr15球化退火的影响。
2) spheroidization annealing
球化退火
1.
To research the spheroidization annealing process of SWRH72B,special alloy steel A and B steel wire for metal card clothing.
对SWRH72B、金属针布专用合金钢A和B 3种钢丝的球化退火工艺进行研究。
2.
The spheroidization annealing process ofφ2.
80mm合金钢Ⅱ三种钢丝的球化退火工艺,分别找出了其最佳的球化退火工艺参数；同时分析了球化退火工艺参数对最终碳化物球粒度的影响。
3.
To research the effects of spheroidization process on carbide configuration and distribution and the effects of drawing deformation magnitude on spheroidization annealing microstructure about special alloy steel wire for metal card clothing after drawing deformation.
研究金属针布专用合金钢丝拉拔变形后,球化退火工艺对碳化物形态及分布状态、拉拔变形量对球化退火组织的影响。
3) spheroidize annealing
球化退火
1.
Fracture analysis of φ674 semisteel roller in spheroidize annealing;
φ674半钢轧辊于球化退火中断裂原因分析
2.
The article discusses some influencing factors upon evaluation of zonal carbonization of bearing steel, shows influencing extent attribute to grinding depth, time of etching, spheroidize annealing.
研究了轴承钢带状碳化物评级过程中的影响因素,找出了磨制深度、腐蚀时间、球化退火对其带状碳化物的影响程度,从而来指导实际的评级检验工作,以确保轴承钢的质量。
3.
In this paper,the drawing and spheroidize annealing processes of SWRH57EK SWRH72B SWRH82B high-carbon wire rod was studied.
本文研究了SWRH57B、SWRH72B和SWRH82B高碳钢盘条的拉拔及球化退火工艺，分析了盘条拉拔过程中珠光体组织的变化规律和低温退火过程中渗碳体球化机理，讨论了化学成分、变形量、加热温度及保温时间对球化过程的影响。
4) spheroidal annealing
球化退火
1.
Production of spheroidal annealing of cold rolled 25 steel strip;
25钢冷轧球化退火钢带的生产
2.
To introduce a new process for making needle latch steel wire with diameter range 0 34～0 53mm The technological process consists of patenting-phosphating-cold drawing-spheroidal annealing under Ac 1 point in electrical heating furnace-slight drawing to finished product The theoretical basis and advantages of the main points of new process are emphatically elaborate
该工艺流程是：铅淬火—磷化—拔丝—Ａｃｌ以下电加热连续退火炉球化退火—轻拉至成品。
5) spheroidizing
['sfiərɔidaiziŋ]
球化退火
1.
This article introduces a new process of spheroidizing of quenching and tigh tempering to GCr15.
该工艺比传统球化退火工艺省时、节能、效率高 ,同时符合工艺要求的各项性能指标 ,已在实际生产中得到应
2.
In this paper the spheroidizing annealing process of the cold extrusion workblank of 20Cr steel have been systematically studied.
本文系统地研究了20Cr钢冷挤压毛坯的球化退火过程，选定了亚共析钢节能、省时与球化效果好的热处理工艺，并已用于工业生产，取得了显著的经济效益。
6) prespheroidizing annealing
预球化退火
补充资料：球化退火
分子式：
分子量：
CAS号：
性质：将钢加热到稍低于或稍高于共析钢或过共析钢的温度，然后缓冷下来。目的在于使珠光体内的片状渗碳体以及先共析渗碳体都变为球粒状，均匀分布于铁素体基体中（这种组织称为球化珠光体）。具有这种组织的中碳钢和高碳钢硬度低）。具有它种组织的中碳钢和高碳钢硬度低，被切削性好，冷形变能力大。对工具钢来说，这种组织是淬火前最好的原始组织。
分子量：
CAS号：
性质：将钢加热到稍低于或稍高于共析钢或过共析钢的温度，然后缓冷下来。目的在于使珠光体内的片状渗碳体以及先共析渗碳体都变为球粒状，均匀分布于铁素体基体中（这种组织称为球化珠光体）。具有这种组织的中碳钢和高碳钢硬度低）。具有它种组织的中碳钢和高碳钢硬度低，被切削性好，冷形变能力大。对工具钢来说，这种组织是淬火前最好的原始组织。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条