1) selective melting
选区熔化
1.
Electron beam selective melting of 316L stainless steel powder;
316L不锈钢粉末的电子束选区熔化成形
2) selective laser melting
选区激光熔化
1.
Simulation of the temperature field in rapid prototyping of selective laser melting;
选区激光熔化快速成型过程温度场数值模拟
2.
Laser beam s focused properties and its transmission and transformation in selective laser melting;
选区激光熔化中激光束的传输变换及聚焦特性
3.
Analysis of the morphology of 316L stainless part formed by selective laser melting
选区激光熔化316L不锈钢粉末形貌分析
3) Electron beam selective melting
电子束选区熔化
1.
Effects of powder preheating in electron beam selective melting process;
粉末预热对电子束选区熔化成形工艺的影响
2.
In this study,different kinds of powder were researched on the electron beam selective melting(EBSM-I) apparatus made by ourself.
本研究利用自行开发的电子束选区熔化成形设备进行了316L不锈钢粉末的试验研究,结果发现气雾化粉末具有较好的一维成形能力,但扫描速度不能太快;水雾化粉末聚球现象严重。
4) Selective Laser Melting(SLM)
选区激光熔化(SLM)
5) molten zone
熔化区
1.
The results indicates that the majority of the compounds in molten zone were produced to be τ5(Zr38Cu36Al26),those in the HAZ were ZrCu with small amount of τ5 when the welding speed was 2 m/min,and the compounds existed in HAZ and the molten zone kept amorphous,while the welding speed was 4 m/min,and the formation of any crystalline phases was not detected at the interface,Whe.
采用传统激光焊接技术连接块体非晶合金Zr45Cu48Al7,试验结果显示:焊接速率为2m/min时,熔化区主要生成τ5(Zr38Cu36Al26)相,热影响区主要生成ZrCu相,含有少量τ5相;焊接速率为4m/min时,熔化区保持了非晶特性,热影响区有晶粒生成;当焊接速率8m/min时,热影响区和熔化区均保持非晶特性。
2.
The results indicate that the morphology and the structure in heat-affected zones(HAZs) are different from those in molten zone.
结果表明:在焊接热循环作用下,熔化区和热影响区的晶粒形貌和组织具有很大的差异;焊接速率为2 m/min时,熔化区主要生成5τ(Zr38Cu36Al26)、ZrCu和一未知相,热影响区主要生成ZrCu相;焊接速率为4 m/min时,熔化区保持了非晶特性,热影响区部分晶化,其主要生成相为ZrCu相;热影响区的晶化行为与非晶合金热处理过程的晶化行为有一定的区别,其主要原因是激光焊接时的高速加热及冷却过程对各晶化相生长速率影响程度不同。
6) zone melting
区域熔化
1.
Based on researching on the technique of continuous casting of single crystal metal,this paper puts forward the technique of manufacturing the single crystal metal wire with small diameter,which combines the technique of continuous casting of single crystal mental with the technique of zone melting.
在系统研究单晶连铸的基础上 ,提出小直径线材单晶化技术 ,该技术结合区域熔化技术和连续铸造技术 ,实现了“三个连续” ,即送料连续、加热熔化连续、引锭连续 。
2.
While using zone melting heated mould continuous casting method to produce single-crystal copper wire,the mould temperature field distribution,which is controlled by the different rate of heating power and traction,is the key factor.
利用区域熔化-热型连铸法制备单晶铜线材这项新技术中,能否通过控制不同的加热功率和牵引速度来控制铸型温度场的合理分布是成功生产单晶线材的关键。
补充资料：选区
| 选区 constituency 选举国家权力机关代表（议员）或其他国家公职人员时划分的区域单位，选民开展选举活动和产生代表（议员）的基本单位。现代各国一般都实行区域代表制（又称区域选举制）。即按照地域划分选区，由各选区分别选出本选区的代表（议员） 。选区的划分，通常采取2项原则：①行政区原则。即以行政区（地区）为选区划分的依据。如美国参议员的选举就是按地区划分选区，每州选出2名参议员。②人口分配原则。即按现有人口的多寡，为划分选区的依据。如英国众议员的选举则按人口数划分选区，全国共设 635个选区，每个选区选出1名众议员 。中国的基层选区是按生产单位、事业单位、工作单位和居住状况划分的，基本上实行后一种原则。中国选举法规定，不设区的市、市辖区、县、自治县、乡、民族乡、镇的人民代表大会的代表名额分配到选区，按选区进行选举。西方国家的选区分为大选区制和小选区制两种。大选区制 ，又称多名选区制，指在每个选区选出2名以上代表。小选区制，又称单名选区制，指在每个选区只选出1名代表。选区的划分直接与该国的政党制度有关。两党制的国家一般采用小选区制，而多党制的国家多采用大选区制。 |