1) zinc series
锌系
1.
Preparation of the Enviromental Protected zinc series phosphating solution at room temperature;
环保型室温锌系磷化液的研制
2.
A zinc series phosphating solution was developed by using sodium nitrite as accelerant at room temperature.
研究了磷化液中各组分及工艺条件对磷化膜性能的影响,并分析了锌系磷化的原理。
2) zinc group
锌系
1.
New polyacrylamide flocculants were developed which include a zinc group composite flocculant and a modified polyacrylamide flocculant.
研制出一种锌系复合絮凝剂和改性聚丙烯酰胺絮凝剂。
3) Zn-Ca series
锌钙系
5) zinc components
锌系工件
1.
Relate process,management on the spot,technology parameter,q uality test and environmental requirements of spraying powder paint on the zinc components are discussed.
讨论了锌系工件喷涂的相关工艺、现场管理、技术参数、质量检验和环境要求等。
6) zinc-phosphating
锌系磷化
1.
Aimed at the quality index of weld-neck-connection during 77B coiled-wire-rod online drawing,a fea- sible zinc-phosphating process at high temperature(for short:HZP)was developed.
结果表明,该锌系磷化液具有稳定性高、快速、少渣、使用寿命长和生产成本低等特点;经80℃×(10～15)min喷淋处理后,盘条焊接区可获得膜重>10g/m~2的优质磷化膜,其外观呈均匀黑色,结晶细致,附着牢固,抗蚀性好,能顺利拉拔,满足了当前高强度PC钢绞线原料——77B高碳盘条在线生产所提出的焊接头磷化质量及工艺操作要求。
补充资料：铝-锌系铸造铝合金
分子式：
CAS号：
性质：以锌为主要合金元素的铸造铝合金，是最早获得工业应用的铝合金之一。在工业中应用的Al-Zn系铸造铝合金成分是5％～14％Zn，2％～3％Cu，6％～8％ Si，0.1％～0.7％Mg，并含有少量其他元素。Al-Zn-Cu合金强度较高、切削加工性能和焊接性能良好，但铸造性能和抗腐蚀性能差。Al-Zn-Mg合金具有良好的力学性能和抗腐蚀性能，可以在淬火时效状态下使用，具有更高的强度。另外该合金的熔化温度较高，但其铸造工艺性能较差。Al-Zn-Si合金具有较高的力学性能和良好的铸造性能，广泛用于砂型、金属型和压力铸造。
CAS号：
性质：以锌为主要合金元素的铸造铝合金，是最早获得工业应用的铝合金之一。在工业中应用的Al-Zn系铸造铝合金成分是5％～14％Zn，2％～3％Cu，6％～8％ Si，0.1％～0.7％Mg，并含有少量其他元素。Al-Zn-Cu合金强度较高、切削加工性能和焊接性能良好，但铸造性能和抗腐蚀性能差。Al-Zn-Mg合金具有良好的力学性能和抗腐蚀性能，可以在淬火时效状态下使用，具有更高的强度。另外该合金的熔化温度较高，但其铸造工艺性能较差。Al-Zn-Si合金具有较高的力学性能和良好的铸造性能，广泛用于砂型、金属型和压力铸造。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条