1) manganese dioxide
二氧化锰
1.
Effect of humic substances on the transformation of pentachlorophenol in the presence of manganese dioxide;
腐殖质对二氧化锰引起的五氯酚转化反应的影响
2.
Rapid titration of manganese dioxide content in pyrolusite;
软锰矿中二氧化锰含量的快速滴定
3.
The study on enrichment method of manganese dioxide from manganese slag;
锰泥中二氧化锰富集方法的研究
2) MnO_2
二氧化锰
1.
Creating Ordered Macroporous MnO_2 by Colloidal Crystals Template Methods;
三维有序二氧化锰大孔材料的模板技术合成及表征
2.
Progress on Manufacturing Method of MnO_2 for Battery;
电池用二氧化锰的制造方法及其进展
3.
Structural parameters of MnO_2 and its behaviors of Li~+ and H~+ insertion;
二氧化锰结构参数与嵌Li~+和H~+的行为
3) MnO2
二氧化锰
1.
To improve the capacitance, Li+ as additive was added to (NH4)2SO4 electrolyte for activated carbon and MnO2/ activated carbon hybrid supercapacitor.
在电解液(NH4)2SO4中加入Li+添加剂,用以提高二氧化锰/活性炭混合超级电容器以及活性炭电容器的容量。
2.
This article depicts computer automatism design and method in MnO2 mixture produce course.
叙述二氧化锰混仓生产过程中用计算机实现自动化混仓的设计和实现方法,在计算机控制系统中,采用研华工控机为上位机,西门子PLC S7-200为下位机,用组态王软件作为上位机软件,用梯形逻辑图编写PLC的程序,并给出了通过PLC S7-200的RS485口实现通讯的解决方案。
3.
A new technique with which manganese can be prepared by the electro-deoxidation from MnO2 in NaCl-CaCl2 melt at 850℃ is presented,which has a simple process,low energy cost and no environmental impact.
提出了以二氧化锰为原料经一步熔盐电解得到锰新工艺,具有工艺流程短、低能耗、无环境污染等特点。
4) manganese oxide
二氧化锰
1.
Manganese oxide materials with different crystalline structures and morphologies have been synthesized by a hydrothermal method.
本论文以二氧化锰材料为研究对象,采用水热方法合成一系列不同晶型和形貌的二氧化锰材料;针对其中的层状二氧化锰可插层和可剥离的性质,采用长链烷基铵插层二氧化锰材料为前体,制备聚合物与二氧化锰纳米复合材料,并对其电化学及光学性能进行了研究;采用层板剥离技术,制备二氧化锰纳米片,并以其为构建模块,分别采用静电组装技术和电泳沉积法制备了二氧化锰无机—无机和有机—无机复合薄膜材料。
2.
In this study,oxidative transformation of bisphenol A(BPA) facilitated by manganese oxide(MnO2) was examined in the controlled temperature(25 ℃) and batch experiment using screw-cap glass bottle coupled to completely mixed shaker system.
以室内实验方法,在25℃室温下,以二氧化锰为氧化剂,研究了pH4。
5) MnO 2
二氧化锰
1.
This paper determines different electrode materials?electrolyte concentration?acid concentration temperature and current intensity have effected on the product fractional conversion and product purity in electrolytic oxidation electrolyte solution system by constant current electrolysis manufacturing MnO 2 and also determines the condition C cathode? Pt anode? MnSO 41.
采用恒电流法电解硫酸—硫酸锰混合溶液制备二氧化锰 ,并测定了电解液浓度、酸度、温度以及电极材料对电解产品转化率和纯度的影响。
2.
The relationship between the dus t and MnO 2 concentration in electric welding circumstance is discussed in orde r to calcu late the concentration of MnO 2 from dust concentration.
为探讨电焊作业环境中粉尘与二氧化锰浓度的关系 ,以便于用粉尘浓度推算出二氧化锰浓度。
3.
The effect of adding MnO 2 and plating cobalt on the performance of nickel electrode made of Ni(OH) 2 powder was discussed by means of charge/discharge curve, impedance spectroscopy and cyclic voltammetry.
通过充放电曲线和交流阻抗谱的测定及循环伏安试验 ,探讨了添加二氧化锰和在镍箔上电镀钴层对氢氧化镍粉末压制的镍电极性能的影响。
6) manganic oxide
二氧化二锰
补充资料：二氧化锰
MnO2 一种重要的无机盐工业产品。黑色或灰黑色晶体或无定形粉末。不溶于水，高温下与碳反应生成金属锰。是两性物质，具有良好的吸附性能和较强的氧化能力。
工业上制取二氧化锰的主要方法有：
① 电解法 由锰矿化学加工而得的硫酸锰精制液（浓度为130～207g/l）进行电解,控制电解温度为85～95℃、槽电压 2.5～3V、电流效率90％～95％。二价锰在阳极上被氧化成四价锰并沉积在阳极表面上，将沉积的二氧化锰定期(一般为一个月)剥离下来，经粉碎、洗涤、干燥即得成品。该法所得产品放电性能好，但电耗高，一般生产每吨二氧化锰需耗电7.2～10.8GJ。
② 热分解法 由锰矿化学加工而得的两价锰盐(碳酸锰、硝酸锰或氢氧化锰)在有充足氧和水蒸气的存在下，在温度约为300～350℃的条件下分解、氧化成二氧化锰，经净化即可得成品。
③ 天然二氧化锰矿提纯法 将天然优质软锰矿经选矿、煅烧、化学处理提纯及活化可制得二氧化锰。该法简单、经济，但产品放电性能稍差。
二氧化锰在电池工业中的用量很大，主要用作电池的去极剂，保证干电池的正常放电。利用其良好的吸附性能,用来制造防毒面具。是玻璃的退色剂,在陶瓷、搪瓷生产中用来制造釉药。还可作有机合成的催化剂、油漆的催干剂、火柴的助燃剂等。
工业上制取二氧化锰的主要方法有：
① 电解法 由锰矿化学加工而得的硫酸锰精制液（浓度为130～207g/l）进行电解,控制电解温度为85～95℃、槽电压 2.5～3V、电流效率90％～95％。二价锰在阳极上被氧化成四价锰并沉积在阳极表面上，将沉积的二氧化锰定期(一般为一个月)剥离下来，经粉碎、洗涤、干燥即得成品。该法所得产品放电性能好，但电耗高，一般生产每吨二氧化锰需耗电7.2～10.8GJ。
② 热分解法 由锰矿化学加工而得的两价锰盐(碳酸锰、硝酸锰或氢氧化锰)在有充足氧和水蒸气的存在下，在温度约为300～350℃的条件下分解、氧化成二氧化锰，经净化即可得成品。
③ 天然二氧化锰矿提纯法 将天然优质软锰矿经选矿、煅烧、化学处理提纯及活化可制得二氧化锰。该法简单、经济，但产品放电性能稍差。
二氧化锰在电池工业中的用量很大，主要用作电池的去极剂，保证干电池的正常放电。利用其良好的吸附性能,用来制造防毒面具。是玻璃的退色剂,在陶瓷、搪瓷生产中用来制造釉药。还可作有机合成的催化剂、油漆的催干剂、火柴的助燃剂等。