1) calcium sulphoaluminate
无水硫铝酸钙
1.
Under the process conditions,qualified sulphoaluminate cement clinker can be produced and main mineral composition of cement clinker are calcium sulphoaluminate and dicalcium silicate.
结果表明:用本试验所采用的原料,配料比为m(矾土)∶m(石灰石)∶m(脱硫石膏)=35∶43∶22,煅烧温度为1400℃可烧制成矿物组成为无水硫铝酸钙和硅酸二钙的合格硫铝酸盐水泥熟料。
2) C 4A 3S
无水硫铝酸钙
1.
The influence of P 2O 5 on the formation and hydration properties of C 4A 3S has been studied in this paper.
研究了掺杂P2 O5 对无水硫铝酸钙矿物形成及水化性能的影响。
3) calcium sulfate anhydrate
无水硫酸钙
1.
The effects of different amounts of calcium sulfate anhydrate and different liquid for hardening on the microstructure,the setting time,compressive strength and phase composition of the CSA/α-TCP bone cement were investigated.
研究了无水硫酸钙(CSA)及不同固化液对α-磷酸三钙(α-TCP)体系骨水泥的显微结构、固化时间、力学强度及物相组成等的影响。
2.
The calcium phosphate bone cement was prepared by the introduction of calcium sulfate anhydrate (CSA),the effects of which on the structure and performance of α-tricalcium phosphate bone cement was investigated by means of the thermal analysis,scanning electric microscopy,mechanics performance testing as well as comparative experiments.
将无水硫酸钙(CSA)引入磷酸钙骨水泥(CPC)中,结合热分析(TG-DSC)、扫描电子显微分析(SEM)和力学性能测试等方法,通过对比试验研究了CSA对α-磷酸三钙(α-TCP)体系骨水泥结构与性能的影响。
3.
The effects of different amounts of calcium sulfate anhydrate on t.
无水硫酸钙(CSA)是一种生物相容性好,可降解的潜在的生物材料,本课题首次将CSA引入CPC中,研究了CSA对α—TCP体系骨水泥性能的影响,实验结果表明适量CSA的加入可促进骨水泥的固化,使得固化产物的长径比增加从而提高了固化体的抗压强度。
4) 3CaO·Al 2O 3·CaSO 4·12H 2O
含水硫铝酸钙
5) calcium hydroaluminosulfate
水合硫铝酸钙
6) calcium sulphoaluminate hydrate calcium aluminate sulphate hydrate
水化硫铝酸钙
补充资料：砷酸钙
白色固体（工业品由于含有杂质而呈红色）；化学式Ca3(AsO4)2。相对密度3.62；难溶于水,溶于稀酸;有毒。可由三氧化二砷与石灰反应制得。砷酸钙和它的碱式盐Ca3(AsO4)2·3Ca(OH)2可用作杀虫剂,对棉铃虫、棉象虫有效，其作用是产生反胃、麻痹和休眠。砷酸钙也用作杀鼠剂。