1) roller shell
铸轧辊套
1.
Analysis about thermal stress of roller shell under various roll casting conditions;
不同铸轧条件下铸轧辊套热应力分析
2.
Study of influence of different casting process parameters on temperature field of roller shell;
不同铸轧工艺参数对铸轧辊套温度场影响规律的研究
2) aluminum cast-rolling roller
铝铸轧辊辊套
1.
The temperature changes in the outside and inside surface of aluminum cast-rolling roller shell,the formation of thermal stress in shell and the regularity of change were briefly described in the paper.
简明扼要地分析了铝铸轧辊辊套内外表面的温度变化及辊套内热应力的形成及其变化规律,着重论述了辊套表面热裂纹的形成与扩展,提出了修正辊套表面热裂纹的措施及合理选择抗热疲劳辊套材料的要求,认为32Cr3Mo1V钢是一种较好的抗热疲劳裂纹的辊套专用材料。
3) roll sleeve
轧辊辊套
4) cast iron milling roll
铸铁轧辊
1.
The high nickel chromiun compound cast iron milling roll by infinite cooling and harding has a good performance and wide application milling roll.
高镍铬无限冷硬复合铸铁轧辊是一种性能优良、应用广泛的轧辊,目前,离心铸造是高镍铬无限冷硬复合铸铁轧辊最常用的生产方法,微裂纹是离心铸造无限冷硬铸铁轧辊比较容易产生的一种缺陷。
5) twin roll casting
双辊铸轧
1.
But for twin roll casting alloy,the microstructure changed from dendrite to fibrous deformation structure after several passes hot rolling at 350℃.
轧制后两种合金均具有良好的力学性能,双辊铸轧合金的强度和延伸率均明显高于传统铸造合金的强度和延伸率,两种合金1 mm厚薄带经350℃/10 min均匀化退火后的抗拉强度、屈服强度和延伸率分别为334。
2.
In order to improve the forming property of twin roll casting magnesium alloy sheets AZ31B, homogenizing treatment was carried out at different annealing temperature (300,350,400℃) and the holding time (1,2,3 h).
为提高双辊铸轧AZ31B镁合金薄板的成形性能,在不同退火温度(300、350、400℃)和保温时间(1、2、3h)下对铸轧AZ31B镁合金薄板进行均匀化退火试验。
3.
The influence of heating temperature in annealing treatment on morphology of eutectic carbide in twin roll casting strip of high speed steel was studied.
研究了退火加热温度对高速钢双辊铸轧薄带中共晶碳化物形态的影响·试验结果表明 ,随着加热温度的提高 ,铸轧薄带中的网状共晶碳化物陆续熔断 ,粒状碳化物逐渐增多·当加热温度达到 95 0℃后 ,铸轧薄带中的网状共晶碳化物基本上被粒状碳化物所取代·用汤普森 弗瑞锥其 (Thompson Friedrich)方程 ,对试验结果进行了分析 ,并得出共晶碳化物层片间距的减小为高速钢铸轧薄带中的共晶碳化物的熔断和球化提供了条件
6) twin-roll casting
双辊铸轧
1.
Microstructure of Twin-roll Casting Magnesium Alloy Strip;
双辊铸轧镁合金板坯微观组织特征
2.
The study of new technology on producing wrought magnesium alloy thin strip by twin-roll casting;
双辊铸轧法生产变形镁合金薄带新工艺的研究
3.
Modelling of solidification microstructure evolution of twin-roll casting magnesium strip using cellular automaton
用元胞自动机方法模拟镁合金薄带双辊铸轧过程凝固组织