1)  quick precision casting
快速精铸
2)  High-speed precision casting
快速精密铸造
1.
High-speed precision casting is a new and rapidly-developed precision mental casting technology,this technology has many advantages that can not be compared with other casting technologies,according to these advantages this technology has a widely application prospect.
快速精密铸造技术是一门迅速发展的高新精密金属铸件制造技术,具有其他铸造技术无法比拟的优点,拥有广泛的应用市场。
3)  rapid casting
快速铸造
1.
Rapid casting processes can increase the production efficiency and is suited for the small batch of various complicated components.
介绍快速成形技术和铸造技术相结合的快速铸造技术。
2.
The rapid casting process which is an integration between rapid prototyping and the casting process is introduced,its status and tendency in China and broad is also introduced.
介绍了快速原形技术和铸造技术相结合的快速铸造技术及其国内外的现状和发展趋势。
4)  rapid casting process
快速铸造
1.
The equipment is applied to the rapid casting process of thin-walled complicated casting,because the liquid metal can pour and fi.
将此设备应用于复杂薄壁铸件的快速铸造中,由于金属熔化后可以在真空环境中进行浇注和充型凝固,取得了良好的效果。
2.
Selection of Polymer Material for SLS Prototype for Rapid Casting Process;
面向快速铸造工艺的激光选择性烧结(SLS)工艺制造可以制造可烧蚀的高分子快速原型,结合熔模铸造工艺能够实现金属零件的无模快速铸造。
5)  Quick casting
快速铸造
1.
Quick Casting by Selective Laser Sintering (SLS);
基于选择性激光烧结技术的快速铸造
2.
Quick casting generated by combining RP technology with casting technology is one of major research fields of RM.
RP技术与铸造工艺结合产生的快速铸造 (QC)是 RM的主要研究领域之一。
6)  high-speed roll casting
快速铸轧
1.
ANSYS-based finite element simulation on temperature field of high-speed roll casting process;
基于ANSYS的快速铸轧过程温度场数值模拟
2.
The research of high-speed roll casting plastic deformation simulating are reached on the basis of the elastic-plastic deformation theory.
在弹塑性有限变形理论基础上,对快速铸轧塑性变形仿真建模进行了研究。
3.
The static equilibrium differential equation in casting and rolling zones during high-speed roll casting process is deduced respectively using the slab method.
在此基础上,对快速铸轧进行了虚拟仿真研究,研究结果表明:不增强铸轧辊内、外冷却能力,单纯减薄铸轧板坯厚度即可提高铸轧速度;随着铸轧速度降低与铸轧区增大以及铸轧坯厚度减薄,轧制压力峰值增大;随着铸轧辊径增大,轧制压力提高,因此铸轧机力能设计参数也要相应增大。
补充资料:汽车刹车钳体精铸母模的激光快速成形加工(MEM工艺)
 

1.背景

汽车工业中很多形状复杂的零部件均由精铸直接制得,如何高精度、高效率、低成本地制造这些精铸件的母模是汽车制造业中的一个重要问题。采用传统的木模工手工制作,对于曲面形状复杂的母模,不但效率低、精度低,难以满足生产需要。采用数控加工中心制作,则成本太高。因此,北京殷华激光快速成形及模具技术有限公司与江苏省常州华能精细铸造厂合作,采用快速成形技术中的熔融沉积制造工艺——MEM制造汽车复杂零部件精铸用母模,精铸部分由华能精细铸造厂完成。

2.工艺过程

首先根据汽车刹车钳体精铸母模的二维图纸,采用Pro-E三维实体建模软件,建立其三维实体CAD模型,然后再采用北京殷华激光快速成形及模具技术有限公司开发的Lark'98系统对CAD模型进行数据处理和工艺规划,最后采用MEM工艺制得汽车刹车钳体精铸母模。

3.设备及工艺参数

采用殷华公司生产的YHHP-1007型ABS丝在MEM-250-II上用MEM工艺制作。送丝速度为180mm/min,喷头行走速度35mm/s为,加热温度为275℃,由于该件较复杂,所以采用整体支撑。



图1 奥迪轿车刹车钳体精铸母模的MEM原型(正面)



图2 奥迪轿车刹车钳体精铸母模的MEM原型(背面)

说明:补充资料仅用于学习参考,请勿用于其它任何用途。