1) recrystallized grains
再结晶晶粒
1.
Effects of solution treatment temperature on the recrystallized grains,the second phases,electrical conductivity and tensile properties of cold rolled Al-1.
结果表明:合金在520℃~560℃之间进行固溶处理时,随着固溶温度的升高,其再结晶晶粒尺寸变化不大,而第二相粒子的数量明显减少;且固溶态合金的伸长率也随着固溶温度的升高而增大,560℃固溶后伸长率最大。
2) recrystal grain size
再结晶晶粒尺寸
1.
The recrystal grain sizes were measured by intercept method.
实验采用高压再结晶方法对冷轧15钢进行处理,使用TEM法观察和分析样品的组织形貌,并测量了再结晶晶粒尺寸。
3) static recrystallization grain
静态再结晶晶粒
1.
The following up grain growth with the deformation temperature,holding time and the influence of deformation temperature,deformation value,initial grain size on static recrystallization grain size have been investigated by means of thermal simulator“ Gleeble-1500” for nuclear steel SA508c1 3 The necessary material models for numerical simulation of recrystallization have been establishe
３核电用钢进行了恒温压缩模拟，分析了变形温度、变形程度、原始晶粒直径对静态再结晶晶粒尺寸的影响，另外还研究了晶粒的长大随温度、时间的变化情况。
4) subgrain recovery and recrystallization
亚晶粒回复与再结晶
5) remelt junction
再结晶结
6) intercrystalline recrystallization
晶间再结晶
补充资料：再结晶晶粒长大
再结晶晶粒长大
grain growth of recrystallization
晶，它的表现很象初次再结晶，如图所示。这是一种非均匀长大即反常的晶粒长大现象。蒸 高纯Fe一351箔材于1200‘C真空中退火 时产生的二次再结晶现象 晶粒长大是以降低晶界(表面)能和相邻晶界(表面)张力相平衡的倾向为驱动力而实现的。再结晶完成后的晶粒，通过界面移动产生长大，总的晶界界面能减少，使金属的总能降低。因此，晶粒长大在热力学上是一个自发过程。 一些溶解在固溶体中的杂质原子对再结晶晶粒的长大速率的影响，远大于对一次再结晶晶核长大速率的影响，它使界面迁移的速率降低。不溶解的弥散质点，也阻碍再结晶晶粒的长大过程。 工业上利用第二相质点来控制晶粒的大小。例如灯泡钨丝中含有Tho:质点、钢中含Al:0。或AIN质点、镁中加入微量Zr以及铝中含有MnAi6质点时，均可显著地阻止在加热时晶粒的长大。在烧结制品中的微细石‘嗦扣‘右抑制品粉长女的作用_zajjiejjng Jingli zhongdo再结晶晶粒长大(grain growth。f reerystaz-lization)初次再结晶完成后的晶粒在晶界能的驱动下发生长大的过程。晶粒长大分为均匀长大和非均匀长大两种情况。初次再结晶后一般得到细小的等轴晶粒组织。但即使在完全再结晶材料中，晶粒也不是理想完整的，而是由曲折的界面分开的。另外，在晶粒的长大过程中，会优先长大几个大晶粒，并因此消耗掉一些较小的再结晶晶粒，这种现象，一般称为二次再结