1) As-cast Lead Brass
铸态铅黄铜
1.
The Dynamic Recrystallization Model of As-cast Lead Brass in Quasi-superplasticity Deformation;
铸态铅黄铜准超塑性变形的动态再结晶模型
2.
The quasi-superplasticity of as-cast lead brass was studied by monodirectional elongation experiment.
采用单向拉伸对铸态铅黄铜进行了准超塑性研究。
2) as-cast leaded brass
铸态铅黄铜
1.
Study on quasi-superplasticity deformation behaviour and mechanism of as-cast leaded brass;
铸态铅黄铜准超塑性变形及其机理的研究
2.
It is indicated that as-cast leaded brass without pretreatment can present certain superplasticity at proper condition.
结果表明:此种不经预处理的铸态铅黄铜,在适当条件下具有一定的超塑性。
3) casting lead brass
铸造铅黄铜
1.
The paper presents some results obtained from a research about effects of rare-earth(RE)and boron(B)refining on the microstructure and dezincification corrosion properties of casting lead brass.
研究了加入稀土和硼细化处理对铸造铅黄铜组织和脱锌腐蚀性能的影响。
4) manganese lead casting brass
铸造用锰铅黄铜
5) silicon lead casting brass
铸造用硅铅黄铜
补充资料:铅黄铜
分子式:
CAS号:
性质:在铜锌合金基础上,加入铅的黄铜。按含锌量可分为单相α铅黄铜,两相(α+β)铅黄铜。单相α铅黄铜只能冷轧和热挤,常用的有63Cu-34Zn-3Pb合金,软态的拉伸强度达350MPa,延伸率为45%。具有较高的强度和良好的冷加工性能,有极好的切削性,主要用于仪表和其他机械式仪表上要求切削性极高的零件。两相(α+β)铅黄铜可进行热轧、热挤和冷加工,典型的合金为59Cu-40Zn-1Pb,在550~650℃温度区间具有超塑性,有较高的强度和优良的切削性能,软态的拉伸强度为420MPa,延伸率为45%,是最经济、最常用的铅黄铜。用于制作热矿井和切削加工的零件、螺钉、垫圈、衬套、螺帽、底座、轴承保持器等。
CAS号:
性质:在铜锌合金基础上,加入铅的黄铜。按含锌量可分为单相α铅黄铜,两相(α+β)铅黄铜。单相α铅黄铜只能冷轧和热挤,常用的有63Cu-34Zn-3Pb合金,软态的拉伸强度达350MPa,延伸率为45%。具有较高的强度和良好的冷加工性能,有极好的切削性,主要用于仪表和其他机械式仪表上要求切削性极高的零件。两相(α+β)铅黄铜可进行热轧、热挤和冷加工,典型的合金为59Cu-40Zn-1Pb,在550~650℃温度区间具有超塑性,有较高的强度和优良的切削性能,软态的拉伸强度为420MPa,延伸率为45%,是最经济、最常用的铅黄铜。用于制作热矿井和切削加工的零件、螺钉、垫圈、衬套、螺帽、底座、轴承保持器等。