1) blast furnace slag
高炉炉渣
1.
Alumina content in Nanjing Steel blast furnace slag is up to 19%,which results in worse slag fluidity,higher furnace operating temperature and higher silicon content of hot metal.
南京钢铁集团公司高炉炉渣中氧化铝含量高达19%,因此炉渣流动性变差,高炉被迫采用高温操作,铁水硅含量偏高,影响了高炉的强化。
2.
The measurementand systemat-ic study had been made on chemical components,mineral compositions,mineral structure,viscosity and melting tem-perature of the blast furnace slag.
试验选取生产现场的高炉炉渣作为基准原料,对现场高炉炉渣和高炉初渣的化学成分、矿物组成、矿物结构以及粘度和熔化性温度进行了测定和系统研究。
3.
INBA is a new type of blast furnace slag processing technology,can be converted to high - grade blast furnace slag cement materials,the recycling of slag implementation.
INBA法是一种新型高炉炉渣处理技术,可以将高炉废渣转为高品位的水泥原材料,实现炉渣的再生利用。
2) BF slag
高炉炉渣
1.
The metallurgic characteristic of Tanggang BF slag was researched in laboratory onthe basis of the current production parameters in the paper.
本文以唐钢高炉生产条件为基础,对唐钢高炉炉渣的冶金性能进行了实验室研究,分析CaO/SiO_2、Al_2O_3、MgO 这三个因素对炉渣的冶金性能产生的重要影响,建立其冶金性能的数学模型,并得出炉渣在高Al2O3条件下合理的造渣制度。
3) blast furnace slag
高炉炉渣<冶>
4) blast furnace slag
高炉矿渣
1.
A large quantity of blast furnace slag discharged in Laiwu Steel Company causes serious environmental pollution.
莱钢每年排放大量的高炉矿渣造成了严重的环境污染,利用高炉矿渣生产微晶玻璃受到国内外的广泛关注。
2.
Replacement of pebbles with blast furnace slag for roadbed and road base cannot only solve the problem of transportation and construction cost,but can solve the problem of pollutions caused by abandoned blast furnace slag,which is significant for the alleviating material shortage,increasing the value of slag,comprehensive utilization and protection of the ecological environment.
高炉矿渣代替碎(卵)石作为公路路基、路面基层材料既可解决材料运距长、建设成本高的问题,又能解决被废弃高炉矿渣占用大量土地资源并对环境造成严重污染的问题,对缓解路用材料短缺,提高矿渣价值和综合利用率,以及保护生态环境等方面具有重大意义。
3.
In view of both the understanding of the double-interface sealing system and the basic analysis of the chemical and physical properties of blast furnace slag(BFS),a set of experimental facilities was developed for the simulation of interfacial bonding in cementing,and experimental evaluation was conducted on the performance of blast furnace slag cement system by bond strength simulation test.
基于对双界面封固系统的认识和对高炉矿渣物化特性的分析,研制了用于模拟固井界面胶结的试验装置,利用胶结强度模拟试验等方法评价了高炉矿渣水泥体系的性能。
5) slag
[英][slæɡ] [美][slæg]
高炉矿渣
1.
The flyash and slag, with standard sand as aggregate, were used as principal mat erials to prepare mineral polymer.
以粉煤灰,高炉矿渣为粉体原料,标准砂为骨料,采用振动成型方法,在蒸压釜中蒸压养护9h(养护温度为192℃),制备了矿物聚合材料。
2.
Glass-ceramic was made from the slag of Bao-Steel Corporation in Shanghai by body crystallization.
以宝钢高炉矿渣为原料整体析晶法制备矿渣微晶玻璃,通过DTA确定微晶玻璃的热处理制度,通过XRD确定玻璃的主晶相,利用SEM观察微晶玻璃的显微形貌,并对微晶玻璃的抗折强度进行测试。
6) BF slag
高炉渣
1.
Discussion on alkali discharge of high Al_2O_3 BF slag in Xiangtan Iron & Steel Corp.;
湘钢高Al_2O_3高炉渣排碱能力的探讨
2.
Study on comprehensive utilization of BF slag at Baotou Steel;
包钢高炉渣综合利用途径的研究
3.
Three types of BF slag quenching dry granulation process including drum granulation,air blast granulation and centrifugal granulation(rotary cup atomizer),which have been subjected to industrial test were introduced.
对高炉渣急冷干式粒化的节水、节能和环保效益进行了估算,同时指出了急冷干式粒化技术的难点。
补充资料：高炉炉渣
高炉炉渣
blast furnace slag
go0lu luzha高炉炉渣(blast furnaee slag)高炉炼铁产生的一种副产品，经加工处理，主要用于制作建筑材料。高炉生产过程中，入炉的各种原、燃料经冶炼后，除获得铁水(炼钢生铁或铸造生铁)和副产品高炉煤气以外，铁矿石中的脉石，燃料中的灰分与熔剂融合就形成液态炉渣，其一般温度为145。一1550℃，定时从渣口、铁口排出。通常将从渣口排出的熔渣称为“上渣”，从铁口随同铁水排出的称为“下渣”下渣中往往混有少量铁水(见上渣与下渣)。高炉炉渣的化学成分取决于原料成分、冶炼铁种、操作方法和冶炼过程中的炉况变化(见表l)。高炉炉渣中CaO、MgO、5102和A12O3为主要组成，占总量的95%以上，这4种成分基本可以决定高炉炉渣的冶金性能。攀枝花钒钦磁铁矿含有较多的TIOZ，包头白云鄂博矿含有较多的CaF:，用这些特殊铁矿石冶炼，炉渣中相应的TIOZ、CaFZ较多。除此之外，渣中还含有少量FeO、Mno和CaS以及一些微量化合物，其碱度(CaO/5102)一般为0.9~1.25。高炉冶炼正常进行时，炉渣成分变化不大，但在生产过程中有时需要调整炉料配比，此时炉渣成分相应变化;炉况变化炉渣成分也会改变，例如炉冷时渣中Feo、510:含量会稍有增多。冶炼每吨生铁一般产生炉渣300~600kg，其多少主要由入炉铁矿石的含铁量而定。铁矿石含铁量越少，脉石含量就越多，相应地加入的熔剂和燃料也越多，所以渣量就越大，中国一些地方小高炉利用当地资源炼铁，渣量会超过600kg八，而欧洲的一些高炉使用含Fe量65%左右的炉料，渣量降到185一)燕黝瓢纂馨 250kg八。大量的高炉渣原作为废物由渣罐车运至弃渣展，而今高炉渣多经水淬制成水渣，成为制作矿渣水泥 场倒掉。这种处理方法日积月累，占地甚大且污染环或渣砖等建筑材料的原料。也可用来制造渣棉、铸石和 境，经营管理费用很高，而且往往因渣罐调拨不及时而膨球等。 影响高炉按时出渣、出铁。由于高炉渣综合利用的发 表1高炉渣化学成分(%) 冶炼铁种…eao}M:01:10。…A，20。1 Feo}Mno 15{cao/5102’ j蹂旧阅牛钊于1 38~42}8~9}35~38}8~15}0.5~0.8}0.3~1.010.7~Jl.1}1.05~1.24 铸适生铁}“5一40{“一9}“7一40}8一15}“!5一o·8}0·“了1·“}。·“一1·5}。·”5一，·10 处理方法主要是水淬处理，作为备用方法还有部装入，水由滤网孔排出，水渣脱水后从底部卸出。这 造渣块。种方法装车外运方便，占地面积小。 水淬处理将熔渣用水急剧冷却，使熔渣粒化为高炉渣水淬处理工艺和方法甚多。常用的有拉萨 细小的固体颗粒，即为水渣。水渣脱水后外运，供水泥(RASA)法和英巴(I NBA)法两种。 厂等使用。作为水泥原料对水渣的化学成分及物理性拉萨法。