1) cycle immersion corrosion
周期浸润
1.
The corrosion-resistance properties of Ca-modified weathering steel have been studied by the weight-loss method in the salt spray corrosion test and the cycle immersion corrosion test.
通过盐雾腐蚀实验和周期浸润实验,采用失重法研究了Ca变质处理耐候钢的耐蚀性能,分析了其锈层结构、表面夹杂物形貌与耐蚀机理,结果表明,在盐雾腐蚀实验和周期浸润实验中耐候钢的失重率分别可达到SPHC钢的36。
2) alternate immersion test
周期浸润腐蚀
1.
The corrosion behavior of SiCP/Al composites with different SiCP sizes(220,140,90,70 μm) and different SiCP volume fractions(42%,49%,55%) was investigated by the alternate immersion test.
通过周期浸润腐蚀实验研究了不同SiC颗粒尺寸(70、90、140、220μm)和不同SiC颗粒体积分数(42%、49%、55%)的SiCP/Al复合材料在酸性环境中的腐蚀行为。
3) alternate immersion tester
周期浸润试验机
1.
An alternate immersion tester was developed following requirement of ASTM G44 and HB 5194.
按照ASTM G44周期浸润试验和HB 5194的要求,研制了一种周期浸润试验机。
4) wet-dry cyclic corrosion tests
周期浸润试验
1.
The corrosion behaviors of Q235 and five kinds of weathering steels containing different contents of alloying elements Cu and Cr in simulated ocean atmos-pheric environment were studied using wet-dry cyclic corrosion tests in the solution of 0.
5%的NaCl溶液中模拟海洋大气环境进行周期浸润试验。