1) core-shell emulsion polymerization
核-壳乳液聚合
1.
Several new emulsion polymerization technologies,such as core-shell emulsion polymerization,microemulsion polymerization,and latex interpenetrating polymer networks(LIPN) were i.
介绍了几种乳液聚合新技术,如核-壳乳液聚合、微乳液聚合、乳胶型互穿网络聚合(LIPN)等,并对它们在功能型含氟乳液涂层材料研究中的应用进行了展望。
2.
The fluorinated acrylate emulsion is prepared using core-shell emulsion polymerization technology.
采用核-壳乳液聚合法制备了含氟丙烯酸酯聚合物乳液,讨论了含氟单体——甲基丙烯酸六氟丁酯(HFMA)用量、复合乳化剂体系用量、引发剂用量、N-羟甲基丙烯酰胺(NMA)用量、聚合反应温度、反应时间、搅拌速度对聚合反应最终单体转化率以及乳液聚合稳定性的影响;测试了涂膜的吸水率和乳液的黏度,以考察涂膜的耐水性。
2) core-shell emulsion polymerization
核/壳乳液聚合
1.
The methods to prepare the waterborne silicon-contained polymer,in terms of seed emulsion polymerization,core-shell emulsion polymerization,emulsifier-free emulsion polymerization,microemulsion polymerization,latex interpenetrating polymerization and et al,are discussed.
介绍了种子乳液聚合、核/壳乳液聚合、无皂乳液聚合、微乳液聚合、互穿网络聚合等制备水性含硅聚合物的方法,并对水性含硅聚合物涂料的应用做了探讨。
3) core-shell emulsion polymerization
核壳乳液聚合
1.
In order to improve water-resistant property and weather-resistant property of styrene-acylic composite emulsion,taking styrene and acrylic acid as core monomers,butyl acrylate,acrylic acid and ethylsiloxane as shell monomers,ethylsiloxane modified styrene-acylic emulsion was prepared by semi-continuous core-shell emulsion polymerization.
为提高苯丙复合乳液的耐水性和耐侯性,以苯乙烯、丙烯酸为核单体,丙烯酸丁酯、丙烯酸、乙烯基三乙氧基硅烷为壳单体,采用半连续核壳乳液聚合工艺制备苯丙复合乳液;研究了乳化剂用量、单体配比、有机硅用量等因素对乳液及涂膜性能的影响。
2.
Low temperature self-cross-linking formaldehyde-free binder for pigment printing is prepared by means of core-shell emulsion polymerization.
采用核壳乳液聚合的方法制备低温自交联的无甲醛涂料印花粘合剂。
3.
Styrene and butyl acrylate were used as raw material,and mixed emulsifier of DSB and OP-10 was used as emulsification system,and potassium persulfate was used as initiator and functional monomer-methacrylic acid was introduced to prepare styrene-acrylate latex with pre-emulsified shell monomer and core-shell emulsion polymerization method.
采用粒子设计、聚合物形态的概念,以St为核单体、BA为壳单体,十二烷基苯磺酸钠(DSB)和烷基酚聚氧乙烯醚(OP-10)的混合乳化剂为乳化体系,K2S2O(8KPS)为引发剂,引入甲基丙烯酸(MAA)功能性单体,采用壳单体预乳化的核壳乳液聚合工艺。
4) core-shell polymer emulsion
核-壳聚合物乳液
5) core/shell emulsion polymerization
核壳乳液聚合法
6) Core-Shell structure emulsion
核/壳结构聚合物乳液