1) water solution cross-linked polymerization
水溶液交联共聚法
1.
With crylic salts,kaolin,starch and etc as raw materials,super-absorbent composite were prepared by using a method of water solution cross-linked polymerization.
以混合丙烯酸盐、高岭土和淀粉等为原料,用水溶液交联共聚法制备了复合高吸水树脂材料,研究了引发剂、交联剂、高岭土用量等因素对材料吸水性能的影响,制备得到了吸去离子水、0。
2) aqueous solution copolymerization
水溶液共聚
1.
ABB·HCI NaHSO 3 redox system as initiator,aqueous solution copolymerization of dimethyldiallylammonium chloride(DM) and acrylamide(AM)was developed.
用偶氮二戊腈盐酸盐 (AAB·HCl) -NaHSO3引发剂 ,进行了二甲基二烯丙基氯化铵(DM)———丙烯酰胺 (AM)水溶液共聚合反应 。
3) linked polymer solution
交联聚合物溶液
1.
Effect of cationic Gemini surfactant on the property of the linked polymer solution;
阳离子型Gemini表面活性剂对交联聚合物溶液性质的影响
2.
Measurement of rheological properties of linked polymer solution by different viscometers;
用不同类型粘度计测定交联聚合物溶液流变性质
3.
Study on the shear stability of linked polymer solution;
交联聚合物溶液的剪切稳定性
4) aqueous solution copolymerization
水溶液共聚合
5) aqueous solution of copolymers
共聚物水溶液
1.
The aqueous solution of copolymers change from transparent to opaque when the temperature is above LCST.
采用紫外可见分光光度计(UV)测定了共聚物水溶液的低临界溶解温度(LCST),研究表明,通过改变共聚单体的配比LCST可在18~32℃范围内调节。
6) solution crosslinking
溶液交联
1.
In comparison with the solution crosslinking ,the tensile strength of gelatin films crosslinked with formaldehyde and GTA in the vapor increased from 25MPa to 42MPa,15MPa to 40MPa,but the.
探讨了溶剂、温度及pH值对明胶膜性能的影响,并以甲醛和戊二醛为交联剂,采用溶液交联和蒸汽交联两种方法对明胶膜进行交联改性。
补充资料:联共(布)
“苏联共产党(布尔什维克)”的简称。列宁创建的无产阶级政党。1898年召开第一次党代表大会,成立“俄国社会民主工党”。1903年,第二次党代表大会通过了党纲和党章,选出了党的领导机构,以列宁为首的布尔什维克(多数派)战胜孟什维克(少数派)取得胜利。1912年,第六次党代表大会将孟什维克清除出党,从此布尔什维克成为独立的无产阶级政党。1917年,在列宁的领导下取得十月社会主义革命的胜利,建立第一个无产阶级专政的国家。1918年,第七次党代表大会上改称“俄国共产党(布尔什维克)”,简称“俄共(布)”。1925年,第十四次党代表大会上改称“苏联共产党(布尔什维克)”,简称“联共(布)”。1952年,第十九次党代表大会上改称“苏联共产党”,简称“苏共”。