1) high carbon ferrochrome
高碳铬铁
1.
It analyses the changeable TiO_2 content in chrome ore and the structural form,the balance of Ti,the reaction mechanism of Ti and its existence form in alloys,the affect factor of Ti content in alloys,and benefits and control methods during the process of smelting low titanium high carbon ferrochrome.
分析了低钛高碳铬铁生产过程中铬矿TiO_2含量变化与结构形式,冶炼过程中Ti的平衡、反应机理和在合金中的存在形式,合金含Ti量高低的影响因素,以及效益与控制方法。
2.
It introduces technological condition and result of smelting high carbon ferrochrome with Xinjiang's high melting point and low grade chromes.
介绍了使用新疆高熔点、低品位铬矿冶炼高碳铬铁的工艺条件和结果,实践证踢通过合理地控制操作,可以得到较理想的技术经济指标。
3.
Based on the principle and characteristics of medium frequency furnace, analysis on physical and chemical performance of liner material , better technological economic indexes and benefits of adaptation to 2 tons medium frequemcy furnace for resmelting high carbon ferrochrome are realizde by pilot production and industrialized production.
采用2 t中频炉重熔高碳铬铁,根据中频炉的原理及特点,对炉衬材料的物化性能进行了分析,通过试生产和工业化生产,取得了较好的技术经济指标和经济效益。
2) High-carbon ferrochrome
高碳铬铁
1.
It analyzed interrelations among the carbon, silicon and sulphur in high-carbon ferrochrome, slag basicity and furnace temperature, coke's sulphur influenced on desulphurization are also discussed, many effective measures are taked for lessening sulphur content in high-carbon ferrochrome.
文章从理论上分析了高碳铬铁合金中碳、硅、硫含量的相互关系,炉渣碱度对合金含量的影响,提高炉温对 炉渣脱硫的作用以及焦炭含硫量的影响等。
3) high carbon ferrochrome slag
高碳铬铁渣
1.
Through studying the existence forms of chrome in high carbon ferrochrome slags,we find out that four forms of chrome in slags,such as water-soluble form,acid-soluble form,safety form and residual form,among them,the chrome contents in water-soluble form are lower and however the chrome contents in acid-soluble form achieve 0.
通过对高碳铬铁渣中铬存在形态的研究,揭示了铬渣中的铬主要以水溶态、酸溶态、安全态和残余态四种形态存在。
4) high carbon-Cr iron powder
高碳铬铁粉
5) high chromium cast iron
高碳高铬铸铁
1.
Microstructures of high chromium cast iron for surfacing;
高碳高铬铸铁堆焊合金组织分析
6) low carbon and high chromium cast iron
低碳高铬铸铁
1.
Based on sliding and drum wear test and microstucture examination,the influence of quenching temperature and holding time on wear resistance of low carbon and high chromium cast iron was inuvestigated.
通过滑动和滚筒式磨损试验及金相组织观察,研究了淬火温度及保温时间对低碳高铬铸铁耐磨性能的影响。
补充资料：高碳铬铁
高碳铬铁铬铁按照含碳量分为高碳铬铁、中碳铬铁、低碳铬铁和微碳铬铁。
高碳铬铁：1、牌号及用途
高碳铬铁(含再制铬铁)主要用途有：(1)用作含碳较高的滚珠钢、工具钢和高速钢的合金剂，提高钢的淬透性，增加钢的耐磨性和硬度；(2)用作铸铁的添加剂，改善铸铁的耐磨性和提高硬度，同时使铸铁具有良好的耐热性；(3)用作无渣法生产硅铬合金和中、低、微碳铬铁的含铬原料；(4)用作电解法生产金属铬的含铬原料；(5)用作吹氧法冶炼不锈钢的原料。
2、冶炼工艺高碳铬铁的冶炼方法有高炉法、电炉法、等离子炉法等。使用高炉只能制得含铬在30％左右得特种生铁。目前，含铬高的高碳铬铁大都采用熔剂法在矿热炉内冶炼。电炉法冶炼高碳铬铁的基本原理是用碳还原铬矿中铬和铁的氧化物。碳还原氧化铬生成cr2c2的开始温度为1373k，生成cr7c3的反应开始温度1403k，而还原生成铬的反应开始温度为1523k，因而在碳还原铬矿时得到的是铬的碳化物，而不是金属铬。铬铁中含碳量的高低取决于反应温度。生成含碳量高的碳化物比生成含碳量低的碳化物更容易。3、炼高碳铬铁的原料冶炼高碳铬铁的原料有铬矿、焦炭和硅石。铬矿中cr2o3≥40％，cr2o3/∑feo≥2.5，s<0.05％，p<0.07％，mgo和al2o3含量不能过高，粒度10～70mm，如是难熔矿，粒度应适当小些。焦炭要求含固定碳不小于84％，灰分小于15％，s<0.6％，粒度3～20mm。硅石要求含sio2≥97％，al2o3≤1.0％，热稳定性能好，不带泥土，粒度20～80mm。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。