1) cold and warm extrusion
冷温复合挤压
2) warm/cold compound extrusion
温冷复合挤压
1.
In view of low material utilization of the traditional forming processes for irregular parts with high strength,the warm/cold compound extrusion process was introduced through the process analysis of a typical irregular parts with high strength.
针对高强度异形件传统成形方法材料利用率低、原材料浪费严重的缺点,通过对一种典型高强度异形件的工艺分析,提出了温冷复合挤压工艺方案。
3) combined warm-cold extrusion
温/冷复合挤压
4) compound cold extruding
复合冷挤压
1.
The method of using the technological processes of cutting off and compound cold extruding to form the fiber joint pedestal blanks in one operation were introduced, and the main structure of the die were described.
介绍了利用切断、复合冷挤压工艺一次成形光纤接头底座毛坯的方法、模具结构及毛坯后加工工序安排 ,并分析了采用新工艺后的效
5) cold compound extrusion technology
复合冷挤压技术
6) isothermal-cold coextrusion
等温-冷挤复合成型
补充资料：复合挤压
复合挤压
compound extrusion
fuhe iiya复合挤压(eompound extrusion)冷挤压时金属沿挤压杆和挤压筒之间的空间以及挤压模孔两个相反方向同时流动的挤压方法。典型的杯杆型复合 ;瑜章 己 }p!。，尸 be，尸 d 杯杆型制品复合挤压示意图 1一挤压杆;2一挤压模;3一锭坯挤压如图所示。在挤压过程的第一阶段(a)，锭坯墩粗并充满挤压筒内腔;在第二阶段(b)，变形金属同时流入挤压杆与挤压模之间的环形间隙及挤压模出口处，开始双向流动，挤压力尸达到最大值;在第三阶段(‘)，金属沿上(B，)、下(BZ)两个方向均衡自由地流动，压力变化平稳;到第四阶段(d)，挤压后期留压余(见挤压残抖)(S1)，对杯一杆型制品取S，妻S。及S:>1/Zd;对杯一杯型制品取51)2S。。该法可用于挤压断面为圆形、方形、六角形、齿形及花瓣形制品，也可挤压等断面的不对称制品。