1) hydroxyl acrylic resin
羟基丙烯酸树脂
1.
Polyurethane coatings was synthesized by using polyether polyol,hydroxyl acrylic resin and tolylene diisocyanate(TDI) under the acidic condition at PH value between 5~6.
用聚醚多元醇、羟基丙烯酸树脂和甲苯二异氰酸酯(TDI)反应,通过选择最佳的反应物,调整反应物的最佳配比,选择适当的混合溶剂,在pH值为5~6的酸性条件下,外加复合催化剂、助剂,制备了弹性、强度、耐候性等综合性能良好,贮存稳定的湿固化聚氨酯涂料,讨论了影响湿固化聚氨酯涂料快干的因素。
2.
This paper introduces synthesis technology and technical index of hydroxyl acrylic resin modified by glycidyl tertiary carboxylic eater(E-10)and performances of coatings from the aliphatic acrylic PU resin.
介绍了采用叔碳酸缩水甘油酯(E-10)改性的羟基丙烯酸树脂的合成工艺、技术指标及以其为基料所配制的脂肪族丙烯酸聚氨酯涂料的各项性能。
3.
The high quality high-solids hydroxyl acrylic resins with low viscosity were prepared by free radical polymerization.
采用单体、引发剂溶液同步连续滴加工艺,通过对引发剂用量及聚合反应温度的调控,有效地降低体系粘度并控制体系中羟基的分布,成功地制备了固含量达7 0%以上的高固含量低粘度羟基丙烯酸树脂。
2) hydroxy acrylic resin
羟基丙烯酸树脂
1.
Modification of TDI trimer with butyl glycol has greatly improved its compatibility with hydroxy-containing resins, forming film with hydroxy acrylic resins.
合成的改性物对羟基树脂有极好的相容性,可以与羟基丙烯酸树脂配成涂料。
3) Acrylic polyol resin (high solid acrylic resin)
羟基丙烯酸树脂(高固体分丙烯酸树脂)
4) polyacrylic hydroxyl resin
聚丙烯酸羟基树脂
1.
Factors influencing HDI biuret particle size coated by anionic polyacrylic hydroxyl resin;
影响阴离子聚丙烯酸羟基树脂包覆HDI缩二脲乳胶粒粒径的因素
6) multihydroxyl polyacryla te resin
多羟基聚丙烯酸树脂