1)  component shaping
工件成形
1.
Using the reversible multilevel-speed electromagnetic stirrer,the slurry transfer tool and its coater,the thin plate sample with five steps and the rheocasting mould,all of which are independently developed,a new rheoforming processing of Al alloy with slurry preparation systems and component shaping systems apart was exploited.
采用自主研制的双向多级速电磁搅拌装置、浆料转移工具和涂料、阶梯板流变性能试件和半固态合金压铸模具,开发出一种半固态合金浆料制备系统与工件成形系统分离的铝合金流变成形技术。
2)  forming technology of cup-shaped
盒形件成形工艺
3)  component shaping system
工件成形系统
4)  Cover Forming
覆盖件成形工艺
1.
CAD/CAE Coordination Design of Automobile Cover Forming;
汽车覆盖件成形工艺的CAD/CAE协同设计
5)  unfold the final shape
展平成形工件
1.
In order to unfold the final shape or modify the initial blank,a Constrained Unfolding Algorithm(CUA) based on one-step inverse FEM(Finite Element Method) is proposed.
分别列举了带约束地展平成形工件、带约束地修正初始坯料以及无约束地展平最终构形几个典型实例,它们成功地消除了成形工件展平后的打折单元,提高了初始毛坯构型的质量。
6)  formative conditions to form labor unions
成立工会的形式要件
补充资料:主要射出成形材料成形时应注意事项

■主要射出成形材料成形时应注意事项
品  名 注    意    事    项
PVC
聚氯乙烯
1.  产品种类范围非常广(硬质、软质、聚合物等),成型条件各有不同,从熔融至分
解之温度范围很小,尤须注意加热温度。
2. 附着水分少,但成型周期尽可能减少(50℃~60℃热风干燥)。
3. 成型机方面,与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹,故射出操作后,柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高,特别注意熔融情形。第二级加热温度较高,且尽可能使成形周
期缩短,比较安全。


PA
聚醯胺树脂
1. 成型温度比其它材料高,故采用油加热的成形机较适当。
2. 吸湿性大,必须充分干燥。水分对成型品的品质影响甚大(80℃热风干燥约5~6小时)。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1.  同PE,但成形温度必须较高。熔融温度170℃,超过190℃则流动性大增,则毛边增加,
易产生接缝及凹入情形。


PC
聚碳酸脂
1. 吸湿性比尼龙小,但若有些微之水分存在则成型品产生其它色泽或气泡,故必须密封
干燥同时成形时也须预备干燥(120℃之温度4小时)。
2. 加热温度超过320℃时则产生热分解,成品变色,故特别注意温度调节,又成型时的温度调节也非常重要,须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜(130℃~135℃,1小时程度为准)。

说明:补充资料仅用于学习参考,请勿用于其它任何用途。