说明:双击或选中下面任意单词,将显示该词的音标、读音、翻译等;选中中文或多个词,将显示翻译。
您的位置:首页 -> 词典 -> Nd-TiO2/沸石
1)  Nd-TiO2/zeolite
Nd-TiO2/沸石
1.
Activities of TiO2,Nd-TiO2,TiO2/zeolite and Nd-TiO2/zeolite prepared photocatalysts were evaluated by decolorizing methyl orange(MO) as model compound to photocatalytic degradation under irradiation of high-pressure mercury lamp.
在紫外光的照射下,以甲基橙为光催化降解反应模型化合物,研究了TiO2、Nd-TiO2、TiO2/沸石、Nd-TiO2/沸石光催化剂的活性。
2)  TiO2/zeolite
TiO2/沸石
1.
The TiO2/zeolite doped with each of rare earth ionsLa3+,Nd3+,Yb3+ was prepared from tetrabutyl titanate and rare earth oxide by sol-gel process.
以钛酸丁酯和稀土氧化物为原料,采用溶胶-凝胶法制备了镧、钕和镱稀土离子掺杂TiO2/沸石光催化剂。
3)  Fe-TiO_2/zeolite
Fe-TiO2/沸石
1.
The photocatalytic degradation of Methyl Orange(MO) in the systems of Fe-TiO_2,TiO_2/zeolite and Fe-TiO_2/zeolite photocatalysts under both solar and UV light irradiation was investigated in order to evaluate and distinguish various effects of the Fe and natural zeolite on TiO_2 photocatalytic activity.
分别在紫外光和太阳光照射下,研究了Fe-TiO2,TiO2/沸石和Fe-TiO2/沸石对甲基橙溶液(MO)的光催化分解过程,并通过XRD,AFM,FTIR和吸收光谱等手段,探讨了Fe和沸石对TiO2的光催化活性的影响。
4)  TiO2/clinoptilolite
TiO2/斜发沸石
1.
A series of TiO2/clinoptilolite catalysts(different calcination temperature,different particle size and different loading) were prepared.
制备了一系列TiO2/斜发沸石催化剂(不同焙烧温度、不同粒度和不同负载量),它们在紫外光照射下可降解有机染料罗丹明B(RhB)。
2.
The effect of Cl-and I-on the photodegradation of SRB by TiO2/clinoptilolite and P25 under UV light irradiation was studied.
本文研究了添加Cl-和I-后,在紫外光照射下,对TiO2/斜发沸石和P25光催化降解酸性桃红的影响。
5)  TiO_2/mordenite
TiO2/丝光沸石
6)  TiO2/zeolite catalyst
TiO2/沸石催化剂
1.
With tetrabutyl titanate the titanium source,TiO2 was loaded to the natural clinoptilolite and the TiO2/zeolite catalyst was prepared by using the sol-gel method.
以钛酸四丁酯为钛源,采用溶胶-凝胶(Sol-Gel)法将TiO2负载到天然斜发沸石上,制备了TiO2/沸石催化剂。
补充资料:CaO-TiO2-SiO2 ceramics
分子式:
CAS号:

性质:在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存,性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅,加入少量改性添加剂,经配料、磨细、混合、成型、烧成等工序获得制品,也可先用碳酸钙和二氧化硅高温下合成硅酸钙,用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等,以确保两晶相共存。主要介电性能为:介电常数80~110,介质损耗角正切值(0.8~2.5)×10-4,介电常数温度系数(-450~+550)×10-6/℃。抗电温度(45~55)kV/mm,电阻率(1011~1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。

说明:补充资料仅用于学习参考,请勿用于其它任何用途。