1) solution dipping method
溶液浸渍法
1.
FeS2 thin films were deposited on porous surface of TiO2 on ITO conducting glass by solution dipping method.
采用溶液浸渍法在ITO导电玻璃表面的多孔TiO2薄膜上沉积了FeS2薄膜。
2.
Porous TiO2 films were prepared by sol-gel and Screen Printing method,and ZnO/TiO2 composite films were prepared using solution dipping method.
用丝网印刷结合溶胶凝胶法制备了多孔TiO2薄膜,用溶液浸渍法制备了ZnO/TiO2复合薄膜;对薄膜的热处理制度、表面形貌、横断面结构、吸光度等进行了分析;组装电池,测试了电池的光电性能,结果表明:浸渍Zn(Ac)23 h,经过适当的热处理后,可以形成结晶良好,吸光度较好的ZnO/TiO2复合薄膜,电池的开路电压,短路电流以及光电转换效率均得到较大的提高。
2) solution impregnation
溶液浸渍
1.
A 3D C/SiC-(W-C)composite was prepared by combining chemical vapor infiltration(CVI)technology with solution impregnation method.
采用化学气相渗透(CVI)结合溶液浸渍法制备3D-C/SiC-(W-C)多元基复合材料,利用XRD、SEM技术对材料烧蚀前后的物相组成及微观结构进行表征,并讨论了复合材料的烧蚀性能。
3) impregnating solution
浸渍溶液
1.
Measurement of nickel in impregnating solution by atomic absorption spectrometer;
原子吸收光谱法测定浸渍溶液中高含量镍
2.
The effect of the pH of impregnating solution and the use of additives on the chemical and physical properties of Co-Mo/Al 2O 3 hydrotreating catalyst were discussed.
讨论了浸渍溶液pH以及在浸渍溶液中添加助剂等对Co -Mo加氢催化剂物化性质的影响 ,调整浸渍溶液 pH可以改变催化剂孔结构 ,在浸渍溶液中添加助剂可以改善活性金属在加氢催化剂表面的分布。
4) sol-dipping method
溶胶-浸渍法
1.
The reaction kinetics and mechanism of oxidation reaction of SiO_2 coating/3-D braided carbon fiber prepared by the sol-dipping method were studied systemly through XRD,SEM,isothermal weight-loss and non-isothermal TG-DTG methods.
采用溶胶-浸渍法,在三维碳纤维编织体的纤维表面涂覆SiO2涂层,通过XRD、SEM、等温氧化失重和非等温TG-DTG等测试手段研究了制备方法对涂层完整性的影响,并对涂层/编织体材料(CB)氧化反应的动力学和机理进行了系统研究。
2.
The SiO2 coating on 3-D braided carbon fiber was prepared by the sol-dipping method.
采用溶胶-浸渍法,成功地在三维编织碳纤维的纤维表面涂覆SiO2,并通过碳热还原反应制得厚度约为0。
3.
The SiO2 coating on 3-D carbon fiber braids was prepared by the sol-dipping method.
采用溶胶-浸渍法,在三维碳纤维编织体的纤维表面涂覆SiO_2涂层。
6) Impregnating solution of electrochemistry
电化学浸渍溶液
1.
Determination of high content Cobalt in Impregnating solution of electrochemistry;
电化学浸渍溶液中高含量钴的分析测试
补充资料：氢氧化钠水溶液浸渍试验
分子式：
CAS号：
性质：橡胶耐碱性试验之一。某些生活、医用橡胶制品和橡胶衬里在使用中会经常接触碱性溶液，需进行耐碱性试验。试验时通常将胶样浸在一定浓度的氢氧化钠溶液中，在规定温度下浸泡一定时间，再观察其外观变化情况和试样某些物理性能的变化情况。
CAS号：
性质：橡胶耐碱性试验之一。某些生活、医用橡胶制品和橡胶衬里在使用中会经常接触碱性溶液，需进行耐碱性试验。试验时通常将胶样浸在一定浓度的氢氧化钠溶液中，在规定温度下浸泡一定时间，再观察其外观变化情况和试样某些物理性能的变化情况。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条