1) MgB2 bulk
MgB2块材
1.
It is revealed that the macro-characteristics and the microstructure of the MgB2 bulk,such as the content of the non-superconducti.
03∶2的比例混合、压制成型后,在流通高纯氩气的条件下分别于660、700、750、800、850和900℃烧结1h,制备出MgB2块材。
2) MgB2 superconducting bulk
MgB2超导块材
1.
The single phase MgB2 superconducting bulk was successfully synthesized by SHS ( Self-Propagating High-Temperature Synthesis) , method.
采用自蔓延(SHS)法成功制备了MgB2超导块材,样品单相性好,其临界温度Tc=38。
3) nano SiC doped MgB2 bulks
纳米SiC掺杂MgB2块材
4) MgB2 wires
MgB2线材
5) MgB_2 wires
MgB2超导线材
1.
Phase compositions, microstructure features, chemical components and critical current density (J_c) of the doped and the undoped MgB_2 wires are investigated by using X-ray diffractometer, scanning electron microscopy, energy dispersive spectrometer and the standard four-probe resistance technique, respectively.
以低碳钢管为包套材料,采用原位粉末套管法制备出5mol%TiB2掺杂的MgB2超导线材。
6) Fe-sheath MgB_2 wire
铁基MgB2线材
补充资料：高温超导体块材组织结构
高温超导体块材组织结构
microstructure of the bulk high temperature superconductor
高温超导体块材组织结构mierostrueture of thebulk high temPerature supereonduetor高温超导体的相组成、晶粒形貌和尺寸，以及与超导电性关系密切的冶金缺陷和晶体缺陷。块材是指薄膜和纤维之外的三维大尺寸材料。 1986年以来陆续发现的高临界转变温度Tc超导体是一个具有陶瓷特性的庞大家族。除Tc高之外，还有很多不同于传统低Tc超导体的共同特征:它们大多具u)为化学全部有超;即的多二uo犷望，叮类。晶块为片和铺这些质相卜、杂和原常常1988Zn)、薄膜约晶Cu、杂相 贫a一b超流角为:值。在相目肠样密度匀单靠实有畸变的层状钙钦矿结晶结构;成分多是以铜((主要元素的金属氧化物，氧含量和含铜材料中铜跳价态都具有不确定性;化合物中大多数金属元素司或部分被其他金属元素替代而不明显改变或仍然具导电性;晶体结构和超导电性具有明显的各向异性使在同一种超导体中，往往共生着结构和Tc各异种超导相。BISrCaCuO(BSCCO)、YBa((YBCO)和TIBaCaCuO(TBCCO)系最有实用矛而被研究得最多的是BSCCO和YBCO超导体。 块材晶粒排列从组织形态上块材可分以下了①晶粒随机取向多晶块:晶轴取向呈无规排列的多材。又称颗粒超导体。秘(Bi)系多晶块中的晶粒状，c轴平行于片的厚度方向;忆(Y)、锭(TD(La)系块材晶粒形状类似，为等轴或棒状晶。在多晶材料中，往往含有少量的非超导金属氧化物杂和孔洞。体密度为理论密度的70一95%。晶粒尺二相和孔洞所占的体积分数和分布状态，与制作工艺始粉末粒度、坯料的成分均匀度有关。在晶界附近，可观察到由热加工过程中应力集聚产生的微裂纹。年和1990年，美国的D.拉巴勒斯蒂(LarbalestiD.戴莫斯(Dimos)等人先后分别对忆系烧结块和双晶作了深入的研究。在烧结块中，有75%以上界是清洁无杂相的，其余不到25%的晶界为含富贫Y、贫钡(Ba)和氧(O)的杂相薄层;即使是无的晶界，其两侧snln的短程区也是富Cu、贫BaO的。