1) Acid leaching
酸浸
1.
Study on enrichment of germaniumin hot acid leaching and zinc-smelting with iron vitriol method;
热酸浸出—铁矾法炼锌工艺中富集锗的研究
2.
Investigations into separation of the components such as A1_2O_3 in the gangue by acid leaching;
煤矸石中Al_2O_3等成分的酸浸分离研究
3.
Study on low grade sulfide zinc-lead ore flotation and separation through acid leaching with oxygen pressure;
低品位硫化铅锌矿混合浮选-氧压酸浸分离铅锌的研究
2) Acid-leaching
酸浸
1.
A comparative investigation on the XRD spectra of coal series kaolin and high-SiO 2/Al 2O 3 kaolin before calcining and acid-leaching and after that, clearly shows that these two kinds of kaolins have the same calcining and acid-leaching mechanisms.
用XRD谱图对比了煤系高岭土与高硅铝比高岭土煅烧酸浸前后的结晶分布特征 ,发现两者的煅烧活化过程完全相同 ,只有其中的高岭石经煅烧成为偏高岭石后才能进行酸浸反应 ,后者含有大量的硅铝化合物伴生矿使得最大浸取率很低。
2.
The technological route for the preparation of manganous sulfate from rhodochrosite by acid-leaching was reviewde.
介绍了以菱锰矿为原料，用硫酸浸出法制备硫酸锰的工艺路线，详细讨论了各种因素对锰浸出率及产品质量的影响，进而对老工艺进行了改进，优化出了最佳工艺条件。
3.
Effect of various factors on the kind and concentration of acid,ratio of solid and liquor,amounts of adding HF,temperature and time of acid-leaching were investigated,an.
本文采用混酸加氟法对工业微硅粉进行除铁试验研究,试验研究了酸的种类和质量分数、固液比、混酸配比、氢氟酸的加入量、酸浸温度和时间等因素的影响,结果表明:最佳的工艺条件是混酸的成分为3%HCl+17%H2SO4,液固比为1。
3) Leaching
[英][li:tʃ] [美][litʃ]
酸浸
1.
The paper comprehensive introduce roasting and leaching technology of silica and charcoal based vanadium ore .
试验结果表明,采用无钠化空白焙烧-酸浸工艺,钒的浸出率93。
2.
In this study,we strengthened the effect of leaching process at the temperature above 100 ℃,proper content of HF acid and leaching time,which can further eliminate the impurity element to make high purity quartz power.
针对脉石英矿中含有大量云母及长石等伴生矿的特点,通过调整溶液浓度及温度等手段,强化矿物的酸浸效果。
3.
The optimal parameters for V2O5 extraction from stone coal with the technology of roasting-sulfuric acid leaching is investigated by orthogonal experiments.
采用正交实验研究焙烧-硫酸浸出法从石煤中提取五氧化二钒的最佳条件。
4) acid leach
酸浸
1.
The vanadium phase and valence state of stone-coal with low carbon in Guizhou province were analyzed by electron probe,and a pressure acid leach experiment was carried out.
利用电子探针分析方法对贵州某地低碳石煤中钒矿物和价态进行了分析,并对该矿石进行了加压酸浸试验研究。
2.
The enrichment and recovery of tantalum and niobium through acid leaching and sodium alkali fusing from tungsten residue is studied.
研究了用酸浸与钠碱熔融法从钨渣中富集和回收钽铌。
5) pickling
[英]['pikl] [美]['pɪkḷ]
酸浸
1.
The experiment studied optimize the pickling process conditions of kaolin.
实验研究了酸浸高岭土的优化工艺条件,高岭土与盐酸质量比为1:3,盐酸浓度为6mol。
2.
The best process conditions of pickling and removing impurity were obtained through experiment.
采用改进的全湿法工艺对柳州锌品集团公司生产的氧化锌原料进行了提纯处理 ,通过实验 ,确立了酸浸、除杂过程的最佳工艺条件 ,制备得氧化锌含量为 99。
6) acid pickling
酸浸
1.
The floatation tungsten concentrate is treated by acid pickling to remove phosphonium and carbonate,and its final concentrate is 70.
浮选钨精矿经过酸浸除磷、碳酸盐后,获得混合钨精矿品位为70。
补充资料：酸浸
酸浸
acid leaching
SUGnjln酸浸(a cid leaching)用无机酸的水溶液作浸出剂的矿物浸出工艺。它是化学选矿中最常用的浸出方法之一。硫酸、盐酸、硝酸、亚硫酸、氢氟酸及王水等均可作为浸出剂，其中应用最广的是硫酸。稀硫酸为弱氧化酸，可用于处理含大量还原性组分(如有机质、硫化物、氧化亚铁等)的矿物原料，硫酸价廉易得，设备防腐蚀间题较易解决，硫酸溶液具有较高的沸点，常压下可采用较高的浸出温度。热浓硫酸为强氧化剂，可将大部分硫化矿物转变为相应的硫酸盐。盐酸的反应能力比硫酸强，可浸出某些硫酸无法浸出的含氧酸盐矿物，但盐酸的价格较高，易挥发，劳动条件较差，设备的防腐蚀要求比硫酸高。硝酸为强氧化酸，价格较高，设备防腐蚀要求较高，一般不单独用作浸出剂，常用作氧化剂。中等强度的亚硫酸具有还原性，常用于浸出含氧化性组分的物料(如二氧化锰、锰结核等)，其浸出选择性较高。氢氟酸常用作钮妮矿物原料的浸出剂。王水主要用于浸出贵金属，使铂、把、金转入浸出液中，而锗、钉、俄、铱、银等则呈不溶物留在浸出渣中，然后用相应的方法将它们分离为单一产品。 酸浸可分为简单酸浸、或化酸浸和还原酸浸三类。简单酸浸采用弱氧化酸作浸出剂，用以浸出某些硫化矿物、金属氧化物和某些含氧酸盐矿物。氧化酸浸则采用氧化酸或弱氧化酸加氧化剂作浸出剂，可浸出大部分金属硫化矿物和某些低价金属化合物。还原酸浸采用还原性酸性溶剂作浸出剂，浸出某些高价金属氧化物或氢氧化物。热浓硫酸浸出及热压氧酸浸出金属硫化矿物的过程属氧化酸浸。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。