1) sulfur-free expandable graphite
无硫可膨胀石墨
1.
Preparation of sulfur-free expandable graphite by nitric acid;
用HNO_3制备无硫可膨胀石墨及影响因素探讨
2) sulphur-free expanded graphite
无硫膨胀石墨
1.
Study on preparation of sulphur-free expanded graphite was made using nitric acid and phosphoric acid as steep in strong oxidizing environment.
以硝酸、磷酸为浸泡剂,在强氧化剂的作用下,对无硫膨胀石墨的制备进行了初步研究。
3) low-sulfur expandable graphite
低硫可膨胀石墨
1.
It was found that the used oxidation-intercalation system could produce low-sulfur expandable graphite with good expandable property.
探索了 HCIO_4/H_2SO_4/KMnO_4/CH_3COOH 氧化插层体系制备低硫可膨胀石墨的新方法。
4) low sulfur expansible graphite
低硫可膨胀石墨
1.
The low sulfur expansible graphite was prepared by reacting natural flake graphite with mixing solution made from sulfuric acid(98%), nitric acid(65%) and oxalic acid.
用硫酸（９８％）、硝酸（６５％）和草酸的混合液与天然鳞片石墨反应制备低硫可膨胀石墨，最佳反应条件是：石墨、硫酸（９８％）、硝酸（６５％）、草酸的重量比为１∶２。
6) sulfur-free & anti-oxidation expandable graphite
无硫抗氧化性可膨胀石墨
1.
Therefore,the study on sulfur-free & anti-oxidation expandable graphite preparation has been paid more attention.
早期制备的膨胀石墨产品中残留的硫会腐蚀金属,并且在温度较高,有氧化剂存在的条件下极易被氧化,使密封效果下降,因此无硫抗氧化性可膨胀石墨的研究备受关注。
补充资料：膨胀石墨
分子式：
CAS号：
性质：又称柔性石墨。石墨经特殊化学处理，嵌入碱金属、卤素、金属卤化物、强氧化性含氧酸等形成层间化合物，再经高温处理急速分解，发生膨胀，体积可增至原来的几百倍。疏松多也，富有弹性。耐温范围宽，在-200～3600℃之间。能承受中子、γ-、β-等射线的长期照射。在高温、高压或辐射等条件下工作，不发生分解、变形或老化。化学性质稳定。可作密封元件，可在深冷氢气分离净化装置、硫酸回收装置、核能工业的硼酸泵等苛刻的条件下使用。还可作坩埚、保温、衬里、隔音和防震材料以及催化剂载体、吸附剂、脱色剂等。是有前途的新颖工程材料。缺点是强度还不够高。