1) N-vinyl-2-pyrrolidone(NVP)
N-乙烯-2-吡咯烷酮
1.
To investigate 2-hydroxyethyl methacrylate(HEMA)-co-N-vinyl-2-pyrrolidone(NVP) hydrogel film swelling performance,a series of HEMA-NVP copolymer films are synthesized with HEMA and NVP in different monomer mass ratios under UV lamp at room temperature,using 0.
为探讨甲基丙烯酸-2-羟基乙酯(HEMA)-co-N-乙烯-2-吡咯烷酮(NVP)共聚物水凝胶薄膜的溶胀性能,以2-羟基-甲基苯基丙烷-1-酮(1173)为光引发剂,二乙二醇甲基丙烯酸酯(DEGDMA)为交联剂,用紫外灯在室温下合成不同配比的HEMA-co-NVP共聚物薄膜。
2) N-vinyl-2-pyrrolidone
N-乙烯基-2-吡咯烷酮
1.
In this paper, a kind of pH-sensitive hydrogel, poly [NVP-AA-PEGDA] was synthesized from N-vinyl-2-pyrrolidone (NVP), polyethylene glycol diacrylate (PEGDA) and acrylic acid (AA) through free radical polymerization, in which azobisisobutyronitrile (AIBN) was used as the free radical initiator and N,N?methylene bis(acryl-amide) (BIS) as the crosslinking agent.
聚乙二醇(PEG)与丙烯酰氯反应合成聚乙二醇双丙烯酸酯(PEGDA),然后以PEGDA、N-乙烯基-2-吡咯烷酮(NVP)及丙烯酸为主要原料,N,N'-亚甲基双丙烯酰胺(BIS)为交联剂,偶氮二异丁腈(AIBN)为引发剂,采用自由基聚合法合成了对pH值变化敏感的N-乙烯基-2-吡咯烷酮-丙烯酸-聚乙二醇双丙烯酸酯交联共聚物(poly[NVP-AA-PEGDA])水凝胶。
3) vinylpyrrolidone
[,vinilpirə'lidəun]
N-乙烯基-2-吡咯烷酮
4) NVP
N-乙烯吡咯烷酮
1.
To investigate the influence of NIPAm on the soft contact lenses,HEMA-co-NVP-co-NIPAm ter-polymer,an sensitive hydrogel to temperature was synthesized with NIPAm,HEMA and NVP under UV lamp at room temperature,using mass fraction 0.
5%的二乙二醇甲基丙烯酸酯(EGDM A)为交联剂,常温下用紫外灯合成了N-异丙基丙烯酰胺(N IPAm)/甲基丙烯酸2-羟基乙酯(HEM A)/N-乙烯吡咯烷酮(NVP)三元共聚物;与相同条件下合成的HEM A/NVP共聚物进行了试验对比。
2.
Hydrogel materials was synthesized by radical copolymerization of NVP and HEMA,with azobisisobutyronitrile(AIBN) as an initiator.
以偶氮二异丁腈为引发剂,合成了一系列N-乙烯吡咯烷酮(NVP)/甲基丙烯酸-β-羟乙酯(HEM A)共聚物水凝胶材料。
3.
5% ethylene glycol dimethacrylate(EGDMA)as crosslinker,HEMA-NVP copolymer hydro-gel is synthesized under UV lamp at room temperature.
5%的二乙二醇甲基丙烯酸酯(EGDMA)为交联剂,在紫外光照下合成了甲基丙烯酸2-羟基乙酯(HEMA)-N-乙烯吡咯烷酮(NVP)二元共聚物水凝胶。
5) N-vinyl pyrrolidone
N-乙烯吡咯烷酮
6) poly N vinylpyrrolidone (N PVP)
聚N-乙烯吡咯烷酮(N-PVP)
补充资料：2-吡咯烷酮
分子式：C4H7NO
分子量：85.11
CAS号：616-45-5
性质：无色结晶。熔点24.6℃，沸点245℃，相对密度1.116（25/4℃），折光率1.4870。能与水、醇、醚、氯仿、苯、乙酸乙酯和二硫化碳混溶，难溶于石油醚。
制备方法：通常由γ-丁内酯经氨化而得。另一种制法是以顺酐为原料，经加氢、氨化而得，收率可达90%-92%。
用途：用作溶剂和有机合成中间体。用来制造尼龙-4及乙烯基吡咯烷酮等。
分子量：85.11
CAS号：616-45-5
性质：无色结晶。熔点24.6℃，沸点245℃，相对密度1.116（25/4℃），折光率1.4870。能与水、醇、醚、氯仿、苯、乙酸乙酯和二硫化碳混溶，难溶于石油醚。
制备方法：通常由γ-丁内酯经氨化而得。另一种制法是以顺酐为原料，经加氢、氨化而得，收率可达90%-92%。
用途：用作溶剂和有机合成中间体。用来制造尼龙-4及乙烯基吡咯烷酮等。