1) magnesium alloy sheet
镁合金板材
1.
Influence of intermediate annealing on microstructure and mechanical property of magnesium alloy sheet;
中间退火对镁合金板材组织和性能的影响
2.
The textures of AZ31B magnesium alloy sheets in the conditions of hot rolling, cold rolling and heat treatment were investigated, and its feature and influence to the mechanical property anisotropy were studied.
结果表明:轧制镁合金板材具有主要以基面织构为主的板织构,其基面平行于板面,其他织构组分相对较弱;冷轧后的基极密度中心围绕板横向向轧制方向旋转约18°;冷轧后在300℃热处理对织构分布特征影响不大。
2) AZ31 magnesium alloy sheet
AZ31镁合金板材
1.
Research on drawability of AZ31 magnesium alloy sheet processed by differential speed rolling at room temperature;
异步轧制AZ31镁合金板材室温冲压性能研究
2.
Influence of annealing treatment on microstructure and properties of AZ31 magnesium alloy sheet processed by equal channel angular rolling;
退火处理对等径角轧制AZ31镁合金板材组织与性能的影响
3.
Numerical simulation and experimental study of warm deep drawing of AZ31 magnesium alloy sheet;
AZ31镁合金板材温热冲压数值模拟与实验研究
3) AZ31 magnesium alloy sheets
AZ31镁合金板材
1.
Deformation law of equal channel angular rolling for AZ31 magnesium alloy sheets;
AZ31镁合金板材等径角轧制变形规律研究
2.
①The anlysis on the microstructure of clock rolled AZ31 magnesium alloy sheetsThe evolution of microstructure and texture characteristic of AZ31 magnesium alloy sheets in the clock rolling process were studied.
本文提出了一种镁合金板材轧制新工艺-多向轧制,采用该工艺并结合后续热处理,通过试验研究,分析探讨了多向轧制和热处理工艺参数对AZ31镁合金板材微观组织、晶粒取向和力学性能的影响,论文的主要研究结果如下:①多向轧制AZ31镁合金板材微观组织结构分析研究了AZ31镁合金板材在多向轧制过程中的微观组织演变、晶粒取向变化以及织构特征。
4) ZK60 magnesium alloy sheet
ZK60镁合金板材
1.
Equal channel angular rolling(ECAR) was applied to prepare ZK60 magnesium alloy sheets.
对采用等径角轧制工艺(ECAR)制备的ZK60镁合金板材研究发现,与直接轧制的板材相比,等径角轧制板材的晶粒取向由(0002)基面取向演化为非基面取向,经等径角轧制后,板材晶粒没有得到细化,同时形成了大量的平行排列的细密孪晶,强度明显提高。
5) AM60 magnesium alloy sheet
AM60镁合金板材
1.
AM60 magnesium alloy sheets were prepared by equal channel angular rolling(ECAR),the microstructure and mechanical properties were examined.
采用等径角轧制工艺制备了AM60镁合金板材,并对轧制前后板材的显微组织与力学性能进行了对比。
补充资料：镁铝锌系铸造镁合金
镁铝锌系铸造镁合金
magnesium-aluminium-zinc cast magnesium alloy series
mellUxlnx一zhuzao melhej一n镁铝锌系铸造镁合金(magnesium一alumini-um一Zine east magnesium alloy series)以铝、锌为主要合金化元素的铸造镁合金，可用于砂型和金属型铸造，也可用于压力铸造，具有良好的流动性和焊接性能，热裂倾向性低，但有较大的显微疏松倾向。 中国牌号ZM一5(7.5%一9.0%Al，0.15%一0.5%Mn，0.2%一0.8%Zn，Mg为余量)合金，ZM一10(9 .0%~1 0.2%AI，0.15%一0.5%Mn，0.2%一0.8%zn，Mg余量)合金。zM一5合金为镁铝锌系铸造镁合金的代表，相当于前苏联牌号的M月5合金。合金中杂质为铁、铜、镍、硅、钻等，根据需要可适量加些被。 铝是主要合金化元素并含有锌和锰，通过改变铝、锌含量可改变合金的力学性能、铸造性能及抗蚀性能。铝含量的增加能进一步改善合金的铸造性能和提高合金的强度，但使伸长率和抗腐蚀性能降低。加入少量的锌和锰能显著提高合金的抗蚀性能，还可以提高合金的强度。但锌含量增加会使合金的缩松倾向增加。ZM一5合金的铸态组织由固溶体叔Mg)为基体，沿它的晶界以不连续网状分布着y(Mg‘A13)相，以及分布在固溶体叔Mg)中的Mn一Ai化合物小质点所组成。热处理强化常采用两种规范:(1)淬火(T4):加热到370~380℃保温2一4h，再升温至415士5℃保温12一16h，然后在空气中冷却。(2)淬火时效(T6):淬火后再在175士5℃人工时效16h。ZM一5合金的力学性能见表1。 表1 zM一5合金的力学性能详 镁铝锌系铸造镁合金结晶间隔较大，充型能力良好，铸造工艺性能及物理常数见表2。表2 zM一s合金铸造工艺性能及物理常数}牛粉粉{字朴 镁铝锌系铸造镁合金能铸出外形和内腔形状复杂的铸件，加之镁合金在汽油、煤油、润滑油中很稳定，因而多用于航空工业的燃油系统和润滑系统。还可作为在受冲击载荷时能吸收大量能量的零部件及飞机着陆轮的轮毅。 (杨朴)