1)  biaxial tensile strength
双向拉伸强度
1.
This paper introduces recent studies on biaxial tensile strength of portland cement concrete, which indicate that the biaxial tensile strength is 15%~30% lower than the uniaxial tensile strength.
介绍了"砼双向拉伸强度的研究近况及研究结果,即砼的双向拉伸强度比其单向拉伸强度弱化15%~30%"。
2.
The focal point of this paper is to introduce that the important results of the concrete biaxial tensile strength as well as the application of above results to the thickness design of cement concrete pavement.
主要介绍了水泥砼双向拉伸强度研究的重要结果及其在路面板厚度设计中的应用研究;通过对路面开裂、断板等病害的分析,提出了以砼双向拉伸强度为验算标准的路面板厚度设计建议。
2)  concrete biaxial tensile strength
混凝土双向拉伸强度
1.
In this paper we introduce the calculative formulas of the concrete biaxial tensile strength at home and abroad, and first present our proposing formula.
针对混凝土的特性,由Hill各向异性判据,还导出了由单向拉作试验结果表达的混凝土双向拉伸强度计算公式。
3)  transverse tensile strength
横向拉伸强度
1.
The effects of different process conditions(such as time,temperature,pressure)and volume content of Kevlar on the transverse tensile strength of the composites were discussed.
本文主要对芳纶 /聚丙烯混纤复合材料的横向拉伸性能进行了研究 ,讨论了不同的加工条件 (成型温度、时间、压力 )以及芳纶的体积含量等对复合材料体系横向拉伸强度的影
2.
The effects of different process conditions(such as impregnating time, molding temperature and pressure) and volume content of kevlar on the transverse tensile strength of the composites were discussed.
对单向聚丙烯/芳纶纤维复合材料的横向拉伸性能进行了研究,讨论了压制时间、成型温度、成型压力,以及芳纶纤维的体积含量等对复合材料体系横向拉伸强度的影响。
3.
The effects of different process conditions(such as time,temperature, pressure) and volume content of kevlar fiber on the transverse tensile strength of the composites were discussed.
本文主要对芳纶/聚丙烯混纤复合材料的横向拉伸性能进行了研究,讨论了不同的加工条件(成型温度、时间、压力)以及芳纶的体积含量等对复合材料体系横向拉伸强度的影响。
4)  hoop tensile strength
环向拉伸强度
1.
The existing shortcoming in the test method of hoop tensile strength of RPM pipes with strip-shape sample are discussed in this paper.
针对RPM管环向拉伸强度测试中采用板条状试样所存在的问题 ,理论分析和试验研究表明通过改变试样形状和尺寸可明显改善测试结果。
5)  Radial drawing strength
径向拉伸强度
6)  biaxial tensile
双向拉伸
1.
A method of biaxial tensile testing for metallic sheets;
一种金属箔材双向拉伸试验方法
2.
A new failure criteria was proposed in terms of different failure modes of unidirectional ply of rubber composite and validated by biaxial tensile experimental data of nylon 6 cord/rubber composite.
根据橡胶复合材料单向单层板的失效模式,提出了一个新的复合材料的失效准则,并通过尼龙6-帘线/橡胶复合材料单向单层板的双向拉伸试验数据,对失效准则进行了验证。
补充资料:双向拉伸薄膜
分子式:
分子量:
CAS号:

性质:一种经特殊处理的塑料薄膜。是在低于薄膜熔点、高于玻璃化温度下,对厚膜或平片进行纵向和横向双向拉伸,然后在紧张状态下进行热处理收缩定型而得到的成品。用于拉抻薄膜的树脂原料有聚丙烯、聚乙烯、聚酰胺、聚酯、聚苯乙烯、聚氯乙烯等。其中以双向拉伸聚丙烯薄膜(BOPP)产量最大,其透明度可与玻璃媲美,并具有防潮、机械强度高、尺寸稳定、质轻、无毒、印刷性良好等特点。广泛用于食品、纺织品、日用品的包装材料及复合薄膜的基材、真空镀铝基材、电容器薄膜等。