1) Si phase
Si相
1.
Change regularity of primary Si phase in the Al-Si alloys was analyzed and compared with the Si phase in the ZA27 alloys of same Si/Al in this paper.
分析了Al-Si合金中初生Si相的变化规律,并与相同Si/Al比的ZA27合金中析出的Si相作比较,提出了将Al-Si合金中对Si相的变质工艺应用到ZA27合金中,细化组织中的Si相。
2.
The results showed that changes of Si phase structure and Fe phase structure in solution treatment could be summarized as point passivation,fusing and granulation.
通过金相分析、SEM和EDS等方法,研究AlSi7MgBe铝合金固溶处理过程中Si相和Fe相的变化。
2) eutectic Si
共晶Si相
1.
The effect of the solidified rate on the morphology of eutectic Si and α-Al dendrite was studied by mean of scanning electron microscope(SEM).
利用扫描电子显微镜,研究凝固速度对共晶Si相、α(Al)树枝晶形态的影响。
2.
The results show that with the increase of superheat treatment temperature, the undercooling increases, and the superheat treatment results in remarkable refinement of the α-Al dendrite and the particle or fibre transition of the eutectic Si.
结果表明:随着超温处理温度升高,过冷度增大;熔体超温处理使得α-Al相二次枝晶间距变小,共晶Si相颗粒化和纤维化;相同冷却速率下,熔体中Aln、Sin类原子团簇的类型和大小的变化决定了α-Al二次枝晶间距的减小。
3) liquid phase siliconization
液相渗Si
1.
The high temperature oxidation resistance of the TiAl-based alloy can be obviously improved by liquid phase siliconization through the Al-Si alloy.
使用液相Al-Si合金对TiAl基合金进行表面渗Si处理,可明显增强TiAl基合金的高温抗氧化性,经1273 K,100 h的恒温氧化后,不同的表面涂层使合金在40—100 h之间的氧化速率降低了2个数量级,恒温氧化100 h后的最终氧化皮脱落量也减少3个数量级,液相渗Si使TiAl基合金表面高温抗氧化性能得到大幅度改善,其根本原因是Si与TiAl中的元素Ti结合,降低了Ti的活度,相对增强了涂层中元素Al的活度,而且涂层中Al的绝对含量也得到明显提高,这些均抑制了高温氧化过程中TiO_2的生成,涂层最外层形成了致密的Al_2O_3氧化膜。
4) Al(FeMn)Si phase
Al(FeMn)Si相
5) (Fe,Si) 2B phase
(Fe,Si)2B相
6) morphology of silicon phase
Si相形态
补充资料：无晶界玻璃相的无压烧结Si_(3)N_(4)材料