1) LNBR
液体丁腈橡胶
1.
Epoxy resin was modified with liquid nitrile-butadiene rubber(LNBR),and unidirectional boron fiber/epoxy resin(Bf/epoxy) composites were fabricated with compression molding.
对环氧树脂进行液体丁腈橡胶改性,并采用缠绕无纬布层压成型工艺制备了硼纤维/环氧单向复合材料。
2.
The plasticization of HNBR with liquid HNBR (LHNBR) was investigated and compared to that with liquid NBR (LNBR).
研究了液体氢化丁腈橡胶 (LHNBR)对氢化丁腈橡胶 (HNBR)的增塑效果 ,并且与液体丁腈橡胶 (LNBR)进行了比较。
2) CTBN
液体端羧基丁腈橡胶
1.
CTBN MODIFIED BMI CONSTRUCTION ADHESIVE (Ⅱ)THE FORM AND PROPERTIES OF CTBN MODIFIED 1~#/DACPE;
液体端羧基丁腈橡胶改性双马来酰亚胺结构胶粘剂(Ⅱ)DACPE固化BMI体系胶粘剂的改性及形态结构
2.
Aminopolysiloxane and carboxy terminal butadiene-acrylonitrile (CTBN) were used to modify the epoxy resin system, and the heat-resistant epoxy adhesive cured at room temperature was prepared.
采用氨基硅油和液体端羧基丁腈橡胶(CTBN)对环氧树脂进行化学改性,制备出室温固化耐热环氧胶粘剂。
3) CTBN
端羧基液体丁腈橡胶
1.
Dicyclopentadiene bisphenol diyanate ester(DCPDCE) was modified by CTBN to improve its brittleness.
采用端羧基液体丁腈橡胶(CTBN)对双环戊二烯型氰酸酯树脂(DCPDCE)进行改性。
4) hydroxyl-terminated polybutadiene/acrylonitrile rubber
端羟基液体丁腈橡胶
5) liquid hydrogenated nitrile rubber
液体氢化丁腈橡胶(LHNBR)
6) amine terminated liquid nitrile rubber
端氨基液体丁腈橡胶
补充资料：液体丁腈橡胶
分子式：
CAS号：
性质：平均分子量小于1万的丁腈橡胶，呈液态。以过氧化氢异丙苯-乙二胺四乙酸钠-硫酸亚铁-雕白粉为引发剂，进行乳液聚合，聚合温度200℃，聚合时间4h，过氧化氢异丙苯分两次加入，胶液经真空脱气、凝聚、洗涤、干燥得到液体丁腈橡胶。其分子链中的丁二烯以反式1,4为主，两种链节呈无规分布。液体丁腈橡胶有良好的耐油性和黏着性，可与酚醛树脂、环氧树脂制成粘接力强、回弹性和耐油性好的胶黏剂。也可用作不抽出性专用增塑剂。
CAS号：
性质：平均分子量小于1万的丁腈橡胶，呈液态。以过氧化氢异丙苯-乙二胺四乙酸钠-硫酸亚铁-雕白粉为引发剂，进行乳液聚合，聚合温度200℃，聚合时间4h，过氧化氢异丙苯分两次加入，胶液经真空脱气、凝聚、洗涤、干燥得到液体丁腈橡胶。其分子链中的丁二烯以反式1,4为主，两种链节呈无规分布。液体丁腈橡胶有良好的耐油性和黏着性，可与酚醛树脂、环氧树脂制成粘接力强、回弹性和耐油性好的胶黏剂。也可用作不抽出性专用增塑剂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。