2) sulphuric acid dew point corrosion resistance
耐硫酸露点腐蚀性能
1.
The microstructure,nonmetallic inclusions and the mechanical properties,weldability and sulphuric acid dew point corrosion resistance,atmospheric corrosion resistance and wear resistance of sulphuric acid dew corrosion resistant 12MnCuCr steel plates with minimum yield strength of 295 MPa have been studied.
研究了济钢研制和生产的Ｑ２９５级的耐硫酸露点腐蚀的１２ＭｎＣｕＣｒ钢板显微组织、非金属夹杂物及其力学性能、焊接性能和耐硫酸露点腐蚀性能、耐大气腐蚀性能以及耐磨性。
4) sulfuric acid dew point corrosion
硫酸露点腐蚀
1.
The macro and micro analysises of the leaking tubes of the ND steel economizer showed that the leakage was caused by the sulfuric acid dew point corrosion which started from the weld seam.
经过对ＮＤ钢省煤器管束泄漏管子的宏观及微观分析，表明管子泄漏是首先从焊缝开始的硫酸露点腐蚀引起的；同排同位置的５根管子泄漏是由于其中一根管子发生硫酸露点腐蚀后穿孔喷水所引起的高温稀硫酸腐蚀的结果。
6) the sulfuric acid' dew point corrosion prevention steel
耐硫酸腐蚀用钢
1.
The paper analyses the chemical composition,mechanical properties and anti-corrosion capability of 09CrCuSb—— the sulfuric acid′ dew point corrosion prevention steel.
文章通过对耐硫酸腐蚀用钢09CrCuSb钢的化学成分、力学性能和耐蚀能力的分析,以及和锅炉行业常用钢材的各项性能指标的比较,探讨了09CrCuSb钢在锅炉制造中应用的可能性、必要性及法规的符合性。