1) twin defect
孪晶缺陷
1.
The twin defects in Ce:YAP were investigated by using synchrotron radiation topography and etch figures.
采用同步幅射白光形貌及光学显微形貌等手段研究了Ce:YAP晶体中存在的孪晶缺陷。
2) twinning fault energies
孪晶缺陷能
3) dual defect modes
孪生缺陷模
1.
we studied the crystal structure and found that it produced dual defect modes.
利用特征矩阵方法对这一晶体结构进行模拟计算发现,它可以产生孪生缺陷模,并且其透射率有一定的损失。
4) crystal defect
晶体缺陷
1.
Studies of characteristics of crystal defects in diamond synthesized under different conditions;
不同生长条件下合成的金刚石晶体缺陷的特征研究
2.
Researching crystal defects with atomic force microscope;
利用原子力显微镜研究晶体缺陷
3.
The main type of crystal defects in this sample are dislocations, and some of them belong to the Frank type.
利用同步辐射X射线对人造金刚石晶体缺陷进行了形貌学研究,实验采用了透射 (劳埃 )形貌术和反射形貌术两种方法。
5) coarse grain defect
粗晶缺陷
1.
Analyse of coarse grain defect in aluminium alloy die forgings;
铝合金模锻件粗晶缺陷浅析
6) lattice defect
晶格缺陷
1.
Opinions were put forward that impaired the aging behavior of the basis material was not the photocatalytic effect but the photochemical activity from lattice defect of TiO_2.
提出削弱基体材料耐老化性的不是TiO2的光催化作用,而是TiO2晶格缺陷引起的光化学活性。
2.
The lattice defects in AIN ceramic specimens with different thermal conductivities were observed by TEM.
用透射电镜观察了不同热导率的Ａ１Ｎ陶瓷中存在的晶格缺陷，这类缺陷主要以位错线形式呈现，分布不均匀，大多集中在晶界处。
补充资料：孪晶界
孪晶界
dary twin bour
孪晶界twin boundary一种特殊的晶界。孪上的原子正好座落在相邻两晶粒的晶格位置上。由界上没有显著的原子错排，这种晶界是共格晶界，界能要比一般晶界的低得多。 最常见的共格晶界即为共格孪晶界，界面两侧的位向满足反映对称关系，反映面即称为孪生面。给出不同晶体结构的孪生面。 晶体的孪生面界晶晶曰拍于其昆体友中四一仪晶体结构孪生面面心立方 {111}体心立方 {112}密集六角{1’0I2}LBC么△‘BC昆体 面心立方晶体中的{111}面是按ABC ABCZ的次序堆垛起来的，应用堆垛符号表示，即△△△△△△。如果从某一层起堆垛层序颠倒过来变成;ABA CBA CB或△△△△甲甲甲甲，上下两部分就形成了孪晶关系(见图)。可以看出，所有原子“孪生面上)的第一近邻的数目和距离都和完整晶体相有改变的只是孪晶界面上的第二近邻的关系，它们2心立方的ABC型转化为密积六角的BAB型。 如果孪生的第一个丈括水面扮同师面心立方晶体的孪生关系面没有穿过整个晶体，少就是一个肖克利不全位相当于共格孪晶界的一，阶，称为孪生位错。 孪晶可以在形变过才产生，称为机械孪晶;注能在晶体生长过程或退止程中产生，称为生长孪健退火孪晶。(吴希俊猎得栋治冲呵挝域)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。