1) EVA
乙烯-乙酸乙烯酯共聚物
1.
The influence of filler type,filler level,the initial mixing temperature,mixing time and rotor speed on the properties of TPU/EVA blend was investigated by using a torque rheometer.
采用转矩硫化仪考察填料种类和用量、混炼初始温度、混炼时间和转子转速对热塑性聚氨酯(TPU)/乙烯-乙酸乙烯酯共聚物(EVA)共混物性能的影响。
2.
The ethylene-vinyl acetate copolymer (EVA)/clay nanocomposites were successfully prepared through melt intercalation process.
通过熔体插层制备了乙烯-乙酸乙烯酯共聚物(EVA)/粘土纳米复合材料。
3.
An injection super light blowing material of ethylene-vinyl acetate copolymer (EVA) and ethylene-acrylate copolymer grafted with maleic anhydride (Fusabond), which has good properties to meet the adidas footwear standard requirements, was developed and put into production of the injection molding midsole of adidas sport-shoe.
注射硫化交联发泡成型的乙烯-乙酸乙烯酯共聚物(EVA)与马来酸酐接枝的乙烯-丙烯酸酯的共聚物(Fusabond)超轻发泡材料,其力学性能符合adidas鞋材标准,可用于生产注射adidas运动鞋中底;利用流变仪测定转矩和发泡压力随时间的变化来研究其硫化交联反应和发泡作用的动力学,在转矩上升阶段为一级反应,给出了硫化交联反应的速率常数k为1。
2) ethylene-vinyl acetate copolymer
乙烯-乙酸乙烯酯共聚物
1.
Performance of ethylene-vinyl acetate copolymer/styrene-butadiene-styrene block copolymer compound modified asphalt by dynamic vulcanization;
动态硫化乙烯-乙酸乙烯酯共聚物/苯乙烯-丁二烯-苯乙烯嵌段共聚物复合改性沥青的性能
2.
This paper studied the effects of carbon black(CB)on miscibility of high impact polystyrene/ethylene-vinyl acetate copolymer(HIPS/EVA)and predicted the phase morphological transition of the blending system.
研究了炭黑(CB)对高抗冲聚苯乙烯(HIPS)/乙烯-乙酸乙烯酯共聚物(EVA)共混体系相容性的影响,并预测了共混体系的相形态转变点。
3.
The copolymer(VAA-Eu) of vinyl acetate and europium acrylate is blended with ethylene-vinyl acetate copolymer(EVA) to prepare a blend(EVA/VAA-Eu) film.
以乙酸乙烯酯和丙烯酸铕的共聚物(VAA-Eu)与乙烯-乙酸乙烯酯共聚物(EVA)的共混物(EVA/VAA-Eu)制备薄膜,通过测定荧光光谱和透过薄膜的紫外光辐照度,研究其对紫外光的遮挡和光转换作用。
3) ethylene/vinyl acetate copolymer
(乙烯/乙酸乙烯酯)共聚物
4) ethylene/vinyl acetate
乙烯/乙酸乙烯酯共聚物
5) ethy-lene-vinyl acetate copolymer
乙烯-乙酸乙酯共聚物
6) ethylene vinyl-acetate copolymer
乙烯/醋酸乙烯酯共聚物
1.
The photocrosslinking of ethylene vinyl-acetate copolymer (EVA) containing phosphorus- nitrogen halogen-free flame retardant (EM82) was studied,It found that the EVA/EM82 samples with a thickness of 1.
对磷氮类阻燃剂(EM82)无卤阻燃乙烯/醋酸乙烯酯共聚物(EVA)复合材料进行了紫外光交联研究。
补充资料：乙烯-乙酸乙烯酯共聚物
分子式：
分子量：
CAS号：
性质：由乙烯与乙酸乙烯酯共聚而得的一种热塑性树脂。随着乙酸乙烯酯含量的增加，其弹性、柔软性、粘合性、相容性、透明性、溶解性也提高。乙酸乙烯酯含量小于10%时，比聚乙烯柔软，而冲击强度好，用作重包装袋和薄膜以及注射模塑鞋底、电缆覆层、玩具等。乙酸乙烯酯含量在10%-20%时，透明性良好，耐寒、耐应力裂开，用于制农业薄膜、输血薄膜、医疗用具、导液管等。乙酸乙烯酯含量在20%-40%时，具有良好的粘合性，用作热熔胶粘剂，用于粘书、层压、涂层等。乙酸乙烯酯含量在45%-55%时，弹性良好，用作特种橡胶，与其他橡胶相容性好，加工性也好，可用过氧化物硫化，与硫化橡胶不相上下。乙酸乙烯酯含量在65%-95%时为乳液，可用作纤维、纸张等的胶粘剂。
分子量：
CAS号：
性质：由乙烯与乙酸乙烯酯共聚而得的一种热塑性树脂。随着乙酸乙烯酯含量的增加，其弹性、柔软性、粘合性、相容性、透明性、溶解性也提高。乙酸乙烯酯含量小于10%时，比聚乙烯柔软，而冲击强度好，用作重包装袋和薄膜以及注射模塑鞋底、电缆覆层、玩具等。乙酸乙烯酯含量在10%-20%时，透明性良好，耐寒、耐应力裂开，用于制农业薄膜、输血薄膜、医疗用具、导液管等。乙酸乙烯酯含量在20%-40%时，具有良好的粘合性，用作热熔胶粘剂，用于粘书、层压、涂层等。乙酸乙烯酯含量在45%-55%时，弹性良好，用作特种橡胶，与其他橡胶相容性好，加工性也好，可用过氧化物硫化，与硫化橡胶不相上下。乙酸乙烯酯含量在65%-95%时为乳液，可用作纤维、纸张等的胶粘剂。