1) slow cooling
缓冷
1.
The influence of different preheating temperature and slow cooling after welding on the local welding repairing qualities has been studied in this paper.
研究了不同预热温度和焊后缓冷对Cr3钢轧辊局部堆焊修复质量的影响。
2.
Some solutions,such as change the chemical composition and slow cooling under cover were given,and proved effective in practice.
结果表明,断坯截面存在对称分布的粗晶区和细晶区,铸坯产生断裂的原因是连铸坯浇铸完毕后二冷水喷水量不均匀并且未采取缓冷措施,使铸坯形成了脆性组织上贝氏体,在铸坯的转移过程中,内应力导致脆性组织产生裂纹。
3.
The results show that slow cooling after rolling can prevent the crack caused by hydrogen.
针对热轧棒材的低倍中心裂纹问题,本文通过对热轧结构钢的数据统计和金相断口分析,阐明了低倍中心裂纹的特征和断裂机理, 确定了该缺陷的性质为氢致白点,并通过试验验证了轧后冷却对该缺陷的影响,得出了通过采取适当的缓冷措施可以避免氢致裂纹产生的结论。
2) retarded cooling
缓冷
3) stacking for slow-cooling
堆垛缓冷
1.
The reasonable application of dehydrogenation process of plate is put forward, which is applied liquid dehydrogen and finishing plate stacking for slow-cooling at the same time.
通过对几种钢板除氢工艺的分析，提出钢板除氢工艺的合理配置和选择，即中板生产在液态除氢的同时，应采用成品板堆垛缓冷除氢工艺，从而可有效地保证对氢含量有严格要求的高附加值中板产品的顺利生产。
4) slow cooling rate treatment
缓冷处理
1.
Aiming at substrate cracks in the laser cladding MCrAlY coatings on nickel-based superalloy,technological measures for preventing cracks by slow cooling rate treatment were presented based on the originate mechanism of substrate cracks in the paper.
在分析激光熔覆涂层基体裂纹形成机理的基础上,针对采用激光熔覆技术在镍基合金基体上制备MCrA lY涂层存在基体裂纹的问题,提出了缓冷处理的止裂措施,研究了将熔覆后的涂层置于300℃下保温30m in随炉缓冷和置于已预热至300℃的保温箱中随箱缓冷两种缓冷工艺对基体裂纹的控制行为。
5) Slow cooling pit
缓冷坑
6) heat-retarder
缓冷器
1.
The impact of heat-retarder temperature on the structure and performance of super-high speed HOY fiber was studied.
研究了超高速HOY(高取向丝)工艺中缓冷器温度对纤维结构和性能的影响。
补充资料：α型钛合金热锻缓冷组织