1) α-alumina
α-氧化铝
1.
Preparation and characterization of carbon nanofiber washcoat on macroporous α-alumina support;
大孔α-氧化铝载体上纳米碳纤维层的制备与表征
2.
The influence of F~- on the phase transformation of alumina from metastable phase toα- alumina and microstructure ofα-alumina has been studied by TG/DSC,XRD,SEM measurements in this paper.
运用TG/DSC、XRD、SEM等分析技术,研究了F~-对氧化铝物相转变及α-氧化铝显微结构的影响。
2) α-gibbsite
α-氢氧化铝
1.
Crystal phase of ρ-alumina was determinated by X-ray diffraction;content of α-gibbsite was measured by thermal analysis(including TG-DTA);morphology and size of ρ-alumina particles was determined by scanning election microscopy.
用X射线衍射结构分析测定了ρ-氧化铝的晶相;用热分析(TG-DTA)测定了α-氢氧化铝的含量;用扫描电镜测定了ρ-氧化铝粒子的外貌及大小;用氮气吸附法测定了ρ-氧化铝的孔容、比表面和孔分布。
3) a-alumina microfiltration membrane
α-氧化铝微滤膜
4) nano-sized α-alumina
α纳米氧化铝
5) α-Al2O3 seeds
α-氧化铝晶种
6) α-Al_2O_3 nanocomposites
钠米α-氧化铝
补充资料：α-氧化铝
分子式： α-Al2O3
CAS号：
性质：白色晶体粉末。密度4.0g/cm3。熔点2015℃。沸点2980℃。莫氏硬度8.8。不溶于水。难溶于酸。一般不被化学药品侵蚀。可由水合氧化铝经1200℃灼烧制得。硬度仅次于金刚石和金刚砂。可用于制轴承、砂轮、实验器皿等。刚玉是天然的α-Al2O3，因其中含有少量杂质而有不同颜色。人工高温烧结的氧化铝称人造刚玉，可耐1800℃，常用作高温耐火材料。高纯氧化铝与少量着色物如氧化铬(红色)或氧化铁(蓝色)混合，经高温熔融可制得人造宝石，用作钟表和精密仪器的轴承及装饰品。
CAS号：
性质：白色晶体粉末。密度4.0g/cm3。熔点2015℃。沸点2980℃。莫氏硬度8.8。不溶于水。难溶于酸。一般不被化学药品侵蚀。可由水合氧化铝经1200℃灼烧制得。硬度仅次于金刚石和金刚砂。可用于制轴承、砂轮、实验器皿等。刚玉是天然的α-Al2O3，因其中含有少量杂质而有不同颜色。人工高温烧结的氧化铝称人造刚玉，可耐1800℃，常用作高温耐火材料。高纯氧化铝与少量着色物如氧化铬(红色)或氧化铁(蓝色)混合，经高温熔融可制得人造宝石，用作钟表和精密仪器的轴承及装饰品。