2) in-situ blend polymerization
原位共混聚合
1.
Styrene,surfactant and selected superabsorbent polymers were mixed and the in-situ blend polymerization of styrene was carried out when the initiator benzoperoxide was added.
采用乳液聚合法合成了一系列不同单体组成的高吸水树脂,选取吸水树脂与苯乙烯、表面活性剂组成聚合体系,用过氧化苯甲酰引发进行原位共混聚合,制备遇水崩解型聚苯乙烯,并考察了吸水树脂的种类、吸水倍率对崩解材料崩解性的影响。
2.
Styrene, surfactant and superabsorbent polymers weremixed and the in-situ blend polymerization of styrene was carried out when theinitiator benzoperoxide was added.
将制备的吸水树脂与苯乙烯、表面活性剂(Span-80)组成聚合体系，用过氧化苯甲酰引发进行原位共混聚合，制得遇水崩解型聚苯乙烯。
3) in-situ blending toughness
原位共混增韧
4) in-situ polymerization blending
原位聚合共混
1.
The novel environmental friendly polystyrene blending materials were prepared via in-situ polymerization blending.
本研究通过原位聚合共混,制备了一类新型环境友好的聚苯乙烯共混材料。
5) PMMA/ladderlike PPSQ in-situ blend
PMMA/PPSQ原位共混物
1.
o-Ps lifetime and intensity of PMMA/ladderlike PPSQ in-situ blend sversus percentage of PPSQ showed that some interactions involved between PMMA and PPSQ.
通过分析PMMA/PPSQ原位共混物的自由体积空穴尺寸及总自由体积分数随温度变化的规律可知 :在 3种共混试样中 ,M10的自由体积空穴尺寸及自由体积分数最大 ,故其Tg 最
6) in situ blending materials
原位共混材料
1.
In this paper, polysulfone/MC nylon 6 in situ blending materials were obtained by in situ anionic polymerization, basing on caprolactam melt is a good solvent for polysulfone which may dissolve homoge.
本文利用己内酰胺熔体是聚砜(PSU)的良溶剂,聚砜可均匀溶解在己内酰胺熔体中,通过原位阴离子聚合法制备了PSU/MC尼龙6原位共混材料。
补充资料：苯乙烯-丙烯腈共聚物/聚碳酸酯共混物
分子式：
CAS号：
性质：系由丙烯腈-苯乙烯共聚物与聚碳酸酯组成的共混物，可改善丙烯腈-苯乙烯共聚物的拉伸强度、热变形温度及冲击强度，并有较好的加工性能，耐溶剂性及耐候性，丙烯腈含量为25%的共聚物与聚碳酸酯共混可获得最好的综合性能，丙烯腈含量小于10%的共聚物与聚碳酸酯共混可得到透明材料，透光率可保持90%以上，机械共混法制取，可用于汽车仪表盘、挡泥板、其他外饰件及商用机器、电器制件等。
CAS号：
性质：系由丙烯腈-苯乙烯共聚物与聚碳酸酯组成的共混物，可改善丙烯腈-苯乙烯共聚物的拉伸强度、热变形温度及冲击强度，并有较好的加工性能，耐溶剂性及耐候性，丙烯腈含量为25%的共聚物与聚碳酸酯共混可获得最好的综合性能，丙烯腈含量小于10%的共聚物与聚碳酸酯共混可得到透明材料，透光率可保持90%以上，机械共混法制取，可用于汽车仪表盘、挡泥板、其他外饰件及商用机器、电器制件等。