1) oxidation loss
氧化烧损
1.
The problems such as regenerative reheating furnace needing high coal gas pressure,regenerator jamming,great oxidation loss and furnace control inexactitude are solved by ameliorating technique and strengthening operation management.
针对蓄热式加热炉要求煤气压力大、蓄热室易堵塞、氧化烧损大、炉况控制不精等问题,通过技术改进与加强操作管理得到基本解决,提高了蓄热炉的性能,改善了使用效果。
2.
It is thought by analyses that the cause of piebald wire is reffection diference of light at rough surface which is due to higher temperature and higher O 2 content in furnace in annealing of half finished product to make steel wire oxidation loss,to make steel wire face rough after acid pickling.
分析认为形成“花丝”的原因是半成品在退火时由于炉温过高及炉内富氧造成氧化烧损、酸洗后的钢丝表面粗糙 ,对光的反射与正常表面不一样所致。
3.
As compared with the process technique and metal loss in wire rod production at home and abroad,analysis was made to study the status and cause of oxidation loss and cropping of front and back ends in wire rod production at Pangang.
通过与国内外线材生产工艺技术和金属损耗的对比，分析了攀钢线材生产中氧化烧损和成品切头切尾的现状及产生的原因，并从工艺改进和生产管理等方面提出了控制措施。
2) iron loss rate
氧化烧损率
1.
The iron loss rate of the reheating furnace is 0.
分析了订单化生产对加热炉经济指标造成的影响,湘钢宽厚板厂加热炉比国内先进同类型加热炉氧化烧损率高0。
3) bead burning
轮缘氧化[烧损]
4) Oxidizing roasting
氧化焙烧
1.
The phase transformation and weight loss rate of ludwigite in oxidizing roasting were studied by DTA-TG,isothermal TG and XRD.
利用DTA-TG、恒温TG和XRD测试方法研究了硼铁矿氧化焙烧过程中的相变和失重率。
2.
The arsenolite cinders were treated by the processes of oxidizing roasting-pyrolusite pulp absorption,magnetizing roasting-magnetic separation and acid leaching.
采用氧化焙烧—软锰矿浆吸收、磁化焙烧—磁选、酸浸工艺处理砷华废渣。
3.
Germanium is recovered from gerichened vacuumn furnace slag of Shaoguan smelter using the flowsheet of ball milling neural leaching oxidizing roasting chloridizing distillation hydrolysis.
针对韶冶真空炉提锌产生的富锗渣 ,提出了“球磨 中性浸出 氧化焙烧 氯化蒸馏 水解”工艺回收其中的锗。
5) Combustion oxidation
燃烧氧化
1.
A new method has been developed for determination of sulfur content in methanol by using combustion oxidation coupled ion chromatography.
提出采用燃烧氧化偶联离子色谱法测定甲醇中硫含量的新方法 。
6) oxidation roasting
氧化焙烧
1.
Based on a great deal of researches for recovery of S, Fe and Zn from solid waste, a comprehensive utilization technique, including oxidation roasting-absorptio.
本文综述了从固体废渣中回收利用S、Fe、Zn的大量研究成果,同时考虑到原料来源、处理技术、经济效益等因素,采用氧化焙烧-软锰矿浆吸收、磁化焙烧-磁选、酸浸的方案实现砷华生产废渣的综合利用,并通过进一步的试验探索了设计方案的各项优化工艺参数。
2.
The effects of temperature,time,air frequency and different fluxes on the recovery rate of molybdenum for oxidation roasting on low grade molybdenum ore are discussed.
实验研究了低品位钼精矿在氧化焙烧过程中温度、时间、通氧气次数、不同熔剂对钼的氧化转化率的影响。
3.
Oxidation roasting was a pretreatment technique for low-grade and complex siderite, the parameters of oxidation roasting were important to roasting efficiency.
氧化焙烧是解决低品位复杂难选菱铁矿的有效前处理工艺,氧化焙烧参数对焙烧效果影响很大。
补充资料：烧损
烧损
fire waste
Sh0OSUn烧损(fi re waste)钢在高温状态下因氧化而造成的损耗。从锭坯到成品的整个生产过程中钢要经过多次加热，据测定，每加热一次约有0.5%一2.5%的钢被烧损。烧损不仅造成钢的直接损失，产生的氧化铁皮还降低钢的导热能力，侵蚀炉底耐火材料，恶化炉子操作条件，对轧件顺利咬入和钢材表面质量也产生不良影响。因此，减少金属烧损是钢加热过程中的重要间题。钢的烧损(氧化)过程主要是铁与炉气中的C02、02、H20发生化学反应的过程，其反应式如下: Fe+粤。，一Feo 2-‘一_ 3Fe+202一一Fe3O- ZFe:04+今。:一3FeZo3 -一‘一”’2一‘-一‘一J Fe+CO:一FeO+CO 3Fe+4COZ一Fe3O4+4CO 3FeO+COZ一FesO;+CO Fe十HZO一FeO+HZ 3Fe+4HZO一Fe3O4十4H2 3Fe+HzO一-今Fe3O;+Hz烧损与加热温度、加热时间、炉内气氛和钢的化学成分等因素有关。加热温度越高、高温下停留的时间越长、炉内氧化性气氛愈浓，则加热时的烧损愈多。因此减少烧损的主要措施是，在满足加热工艺的条件下，适当提高加热速度，缩短加热时间;控制炉内气氛，在保证燃料完全燃烧的条件下，减少过剩的空气并防止冷空气的吸入等。此外，采取保护性气体或用保护性涂料也能减少或防止钢的氧化。 (衷康)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。