1) residual rare earth
残余稀土量
1.
Too high residual magnesium content, and especially too high residual rare earth content is the main reason causing reverse chill defect.
引起反白口的主要原因是残余镁量,特别是残余稀土量过高,防止措施是采用稀土含量较低的球化剂,提高球化处理温度和浇注温度。
2) remainder rare earth eleme nts
残余稀土
3) residual amount of Rare Earth
稀土残留量
1.
and the range of residual amount of Rare Earth △RE in compacted graphite cast iron treated with mischmetal and R24 .
并在此范围内两者的蠕化率都与稀土残留量有线性关系。
4) residual clay
残余粘土
5) residual soil
残余土壤
6) residual clay
残余黏土