1) internal quality of slab
板坯内部质量
1.
The effects of improvement on internal quality of slab by the dynamic soft reduction at An-gang were introduced.
介绍了安钢采用动态轻压下技术改善板坯内部质量的效果,并分析了动态轻压下对中心偏析和内部裂纹的影响。
2) quality of slab
板坯质量
1.
The results showed that the quality of slabs cast under unsteady conditions is poorer than that cast under steady condition.
00×10-6,相同工艺条件下,该板坯质量处于较高水平。
3) slab quality
板坯质量
1.
Based on those results,an integrated evaluation for slab quality is carried out,and some improvement measures for slab quality are put forward accordingly,which will provide a theoretical gist fo.
结合本溪钢铁集团公司连铸板坯质量存在的问题,应用大样电解、金相分析、扫描电镜能谱分析等检测手段,对选定典型钢种(Q235)铸坯中夹杂物的质量分数、形态及组成,铸坯中气体等进行了分析和综合评价,并提出了改善铸坯质量的具体措施,为进一步提高本钢连铸坯质量提供了理论指导依据。
4) quality of continuous casting slab
连铸板坯质量
5) internal quality
内部质量
1.
Effects of Extrusion Pressure on Internal Quality of Semi-solid Hypereutectic High Chromium Cast Iron Extrusion Parts
挤压力对过共晶高铬铸铁半固态挤压件内部质量的影响
2.
The influence of the soft reduction parameters on the internal quality of heavy rail steel bloom is analyzed,which include center looseness and cen- tral segregation etc.
针对攀钢大方坯连铸机投产初期引进的轻压下装备技术冶金效果不明显、重轨钢铸坯中心疏松、中心偏析等内部缺陷较严重的问题,开展了优化重轨钢连铸轻压下工艺的现场试验,对比研究了轻压下工艺对重轨钢铸坯中心疏松、中心偏析等内部质量的影响,建立了适应重轨钢要求的动态轻压下工艺技术。
3.
Considering the equipments of Masteel,aim at the effect of continuous casting process parameters on internal quality of high carbon steel billet,via strengthen slag-stop during tapping,optimize de-oxidize process,suitable control the superheat,adjust the casting speed,the second cooling water flow rate,the parameter of the M-EMS,etc.
结合马钢的工艺装备,针对连铸高碳钢小方坯内部缺陷的成因,在生产中通过强化出钢挡渣,优化脱氧工艺,加强连铸控制,合理控制过热度,合理调整拉速、二冷水量、电磁搅拌参数等,有效改善了高碳钢小方坯的内部质量。
6) inner quality
内部质量
1.
The present paper analyzes the effect of different electromagnetic stirring intensities on the inner quality of the heavy rail steel bloom through comparison of the results out of different experiments.
采用对比试验研究的方法分析不同电磁搅拌强度下对重轨钢大方坯内部质量的影响,试验中采用搅拌电流分别为250、350、400、450和500A,浇铸的铸坯均为24块。
补充资料：1350mm双流板坯连铸机(重庆钢铁设计研究院设计)
1350mm双流板坯连铸机(重庆钢铁设计研究院设计)
叠 135Omm双流板坯连铸机(重庆钢铁设计研究院设计)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。