1) ultramicro molybdenum nitride
超微氮化钼
1.
Using the high-energy mechanochemistry ball mill of self-designing,the ultramicro molybdenum nitride powder are prepared through the ball-mill reaction of molybdenum and ammonia at room temperature.
利用自行设计的高能机械化学球磨机,在室温下通过使钼粉在NH3气氛下高能球磨得到了超微氮化钼粉体。
2) molybdenum carbide ultra-micron powder
超微碳化钼粉末
3) molybdenum nitride
氮化钼
1.
Synthesis and characterization of an environmental protection catalytic materials molybdenum nitride;
环保型催化材料氮化钼的合成与表征
2.
Preparing ultramicro molybdenum nitride powders by high-energy mechanochemistry method;
高能机械化学法制备超微氮化钼粉体
3.
Research progress in deep hydrodesulfurization by molybdenum nitride catalysts;
氮化钼深度加氢脱硫催化剂研究进展
4) Nd-MoN
钕-氮化钼
1.
Preparation and Conductivity of Nd-MoN by Rare Earth Gas Phase Permeation;
稀土气相扩渗法制备钕-氮化钼及其导电性
5) molybdenum oxynitrides
氧氮化钼
1.
MCM41 supported molybdenum oxynitrides catalyst was prepared by nitriding MoO 3/MCM41 under NH 3 atmosphere at 700 ℃ for 3 h, in which process MoO 3/MCM41 was prepared via thermal spreading the mechanical mixture of MoO 3 and MCM41.
将MoO3和介孔材料MCM 41的机械混合物热处理得到MoO3/MCM 41复合体 ,将MoO3/MCM 41在氨气氛中于 70 0℃氮化处理 3h ,制备了氧氮化钼负载的MCM 41催化材料。
补充资料：超低钼高纯石墨
超低钼高纯石墨是生产信息领域及日常家用小型电器中广泛使用的碱性高能电池的主要原料，是国际上八十年代石墨深加工先进的代表性产品之一。
科学技术发展迅速，产品更新频繁，在世纪之交，日本、美国、德国已率先采用膨胀石墨取代了超低钼高纯石墨（天然磷片）。其原因是：天然磷片超低钼高纯石墨虽有优良的导电性能，但与二氧化锰的粘结性差。采用膨胀石墨制备的碱锰电池，与用超低钼高纯石墨制备的电池相比较，其1500ma大功率放电时间可提高20-30%。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条