1) surface coating treatment agent
表面包覆处理剂
2) surface additives
表面包覆剂
1.
The results showed that it is good use of the Compound surface additives, get the Capability of floating Aluminiumpasten about: The D50 10-20 μm,water coverage is 2.
采用新型的高能研磨方法制备漂浮型铝银浆,研究了研磨工艺、设备和表面包覆剂对产品性能的影响,结果表明,采用复合包覆剂效果较好,漂浮型铝银浆平均粒度D5010-20μm,水遮盖面积2。
3) surface treating agent
表面处理剂
1.
The surface treating agent for rubber shoe sole was synthesized by grafting modification of CR/SBS with methyl methacrylate and acrylic acid.
采用甲基丙烯酸甲酯、丙烯酸接枝改性CR/SBS ,合成橡胶鞋底表面处理剂 ,解决了传统橡胶鞋底粘接强度不大等问题。
2.
The soles of shoes made of ethylene vinylacetate, or EVA sole for short, need surface treating agent for promoting their adhesion.
采用甲基丙烯酸甲酯、丙烯酸接枝改性 SBS,合成 EVA表面处理剂 ,解决 EVA鞋底粘合的问题 。
4) surface treatment agent
表面处理剂
1.
Preparation of acrylic ester copolymer of EVA surface treatment agent;
水性丙烯酸酯共聚物EVA表面处理剂的合成
2.
The surface treatment agent for TPR;
TPR表面处理剂的研制
3.
Preparation of Water-borne Acrylicester Copolymer of EVA Surface Treatment Agent and Laminating Adhesive;
水性丙烯酸酯共聚物EVA表面处理剂及复膜胶的合成
5) surface modifier
表面处理剂
1.
The effects of the contents for fly ash,the surface modifiers for fly ash on the mechanical,flow performances and the heat-durability of the fly ash/polyethylene were investigated.
探讨了粉煤灰的不同含量、粉煤灰的表面处理剂对粉煤灰/聚乙烯复合材料力学性能和流动性、耐热性的影响。
6) coating
[英]['kəʊtɪŋ] [美]['kotɪŋ]
表面包覆
1.
Through the thermodynamic anal ysis of coating process,it was proved that Al(OH)3 nucleus coating Ti(OH)4 c ompetes with Al(OH)3 film coating Ti(OH)4.
热力学分析表明,在纳米Ti(OH)4表面包覆Al(OH)3的过程中,存在核包覆和膜包覆的竞争;而在其它条件不变的情况下,包覆物的过饱和度对包覆形态起到了决定性的影响。
2.
Through the thermodynamic analysis of coating process, it was proved that Al_2O_3 nucleus coating TiO_2 competes with Al_2O_3 film coating TiO_2.
热力学分析表明,用化学液相沉积法在纳米TiO2表面包覆氧化铝的过程中,存在核包覆和膜包覆的竞争;而在其它条件不变的情况下,包覆物的过饱和度对包覆形态起到了决定性的影响。
3.
Studies were focused on the effects of different amounts of cobalt coating on structure and electrochemical characteristics of Ni(OH)_2.
通过“管道式合成”工艺制备了球形氢氧化镍,然后以化学沉积法在氢氧化镍表面包覆氢氧化钴,制备了表面覆钴含量不同(0。
补充资料：表处理语言
表处理语言
list processing language
b 100 ehuli yuyan表处理语言(list pn祀侧弥ing langUage)一类用于描述表及其处理的程序设计语言。表是一种特殊数据集，它是由若干个(包括零个)元素组成的序列。此种数据结构灵活、方便、通用。 表处理的基本操作有:将新元素插人表的指定位置中;访问表中任一元素;删除表中指定位置的元素;将两个表链接成一个新表;将一个表拆成两个表;判断指定表是否空。 第一个表处理语言是1958年由A.Newell等研制的IPI，V。最典型的表处理语言是1960年由J.M改兔rthy及其研究小组设计实现的LISP。其它表处理语言还有Slip，P呼2等。70年代末以来出现了几十种LISP版本，并建立了国际标准G刃~nUSP。在面向对象技术热潮推动下，1988年美国学者将当时若干有代表性的LISP合并为C以万，使之成为AJ领域重要的语言。