1) finish cooling temperature
终冷温度
1.
It was found that the mechanical properties were especially sensitive to the finish cooling temperature.
通过两阶段控轧+快速冷却,综合利用细晶强化、相变强化和析出强化等强化机制获得了分别满足GB/T 16270-1996中Q690和Q620要求的高强度工程机械用钢;着重研究了终冷温度对试验钢显微组织和力学性能的影响。
2) final cooling temperature
终冷温度
1.
Various final cooling temperatures have influence upon mechanical properties of low carbon bainitic steel.
不同终冷温度对低碳贝氏体钢的力学性能有较大影响,金相分析的结果表明其组织的差异导致了力学性能的不同,并简单分析了组织对性能的影响机理。
2.
GCr15 bearing steel rod was investigated to analyze the influence of UFC(ultra fast cooling) final cooling temperature on its structure and microhardness.
以GCr15轴承钢棒材为研究对象,研究了超快速冷却终冷温度对其组织性能的影响。
3.
Effect of cooling rate and final cooling temperature on microstructure and mechanical property in an untra-low-carbon bainitic steel was studied by using hot simulator and laboratory mill test.
采用热模拟试验和实验室轧钢试验,研究了超低碳贝氏体钢在冷却过程中冷却速率和终冷温度对微观组织和力学性能的影响。
3) finishing cooling temperature
终冷温度
1.
The effects of technological parameters,such as finishing rolling temperature and finishing cooling temperature,on the microstructure and hardness of X80 pipeline steel were analyzed in the conditions of controlling the parameters and keeping the cooling rate of 17 ℃/s.
通过控制不同的终轧温度和终冷温度,并在17℃/s冷却速度下控制冷却,研究其对管线钢显微组织和显微硬度的影响。
4) Terminal temperature
冷冻终温
5) precooling end-temperature
预冷终温
1.
Vacuum precooling of strawberry were carried on at precooling end-temperature of(2 ℃),4 ℃ and 6 ℃ respectively,with the un-vacuum precooling as control.
分别以2、4、6℃作为预冷终温对草莓进行真空预冷,以不预冷草莓为对照试验,研究了不同预冷终温对草莓生理生化变化的影响,并记录了草莓预冷过程中果实表面温度、内部温度及真空压力(绝对压力)的动态变化。
6) finishing rolling temperature
终轧温度
1.
The effect of finishing rolling temperature on banded structure of 16Mn steel plate;
终轧温度对16Mn钢板带状组织的影响
2.
Influence of finishing rolling temperature on microstructure and properties of Q450NQR1 high strength weathering steel
终轧温度对高强度耐候钢Q450NQR1组织和性能的影响
3.
By using controlled rolling and cooling,optical and electron microscopy observation,mechanical test etc,the microstructure of hot-rolled 60Si2CrVAT rolled with different finishing rolling temperature,and the effect of hot rolled structure on the microstructure and properties of heat treated products were studied.
以铁路用弹簧钢60Si2CrVAT为研究对象,通过工业控轧控冷试验,采用光学、电子显微技术和力学分析等方法,系统研究了在不同终轧温度下热轧态的组织结构以及对其热处理后组织性能的影响。