1.
The corrosion rate was determined by the weightless method and the inter-phase corrosion mechanism of the cast irons in corrosion medium was studied by the electrochemistry.
用定向凝固技术制备Ｃｒ系白口铸铁，用提取相表面富集法制备碳化物试样，用失重法测定样品的腐蚀失重率，并通过电化学法探讨Ｃｒ系白口铸铁在腐蚀介质中的动态相间腐蚀机理。
2.
The inter-phase corrosion mechanism of hypo-eutectic chromium white cast irons is divided into the primary and secondary original cells according to the couple corrosion principles.
为了探讨铬系白口铸铁在腐蚀介质中的相间腐蚀机理 ,对试验合金应用定向凝固技术 ,采用提取相表面富集法制备了碳化物试样 ;依据电偶腐蚀原理 ,建立了亚共晶铬系白口铸铁相间腐蚀原电池模型 ;测定了试验合金组成物偶接前、后的腐蚀速度 。
3.
The corrosion rates have been determined by the weightless and the inter-phase corrosion mechanism of chromium white cast irons in corrosion medium has been studied by the electrochemistry.
应用定向凝固技术制备了Ｃｒ系白口铸铁，采用萃取法制备碳化物试样，用失重法测得腐蚀速率，并通过电化学法探讨Ｃｒ系白口铸铁在腐蚀介质中的相间腐蚀机理，结果表明：（１）Ｃｒ系白口铸铁在腐蚀介质中存在严重的相间腐蚀，相间腐蚀失重率占合金总腐蚀失重率的一半以上；（２）碳化物的电化学行为不同于合金和基体，一直处于自钝化状态，Ｍ７Ｃ３型碳化物比Ｍ３Ｃ型更耐蚀、更稳定；（３）碳化物与基体两相间的腐蚀电位差是相间腐蚀的驱动力，在此腐蚀过程中，碳化物被保护，基体被加速腐蚀，提高基体的腐蚀电位，不仅可以降低相间腐蚀速率，而且能够大幅度提高 Ｃｒ系白口铸铁的耐蚀性。
5) Metallographic Etch
金相腐蚀
1.
Metallographic Etch for Cast AZ91D Magnesium Alloy;
铸造镁合金AZ91D金相腐蚀方法研究
6) corrosion/σ-phase
腐蚀/σ相
补充资料：多相流计量
多相流计量
multiphase flow measurement
r IJ口口，一‘-‘产，.，duo汉iangliu 11110叩多相流计t(multiphase flow~uremeni)同时包含两种或两种以上物质并且有明确分界面的流体，称为多相流。例如，水和冰、空气和水、气体和固体、液体和固体等均为两相流，水、气和油为三相流，水、气、油和沙为四相流。多相流应用范围很广，但流体力学上的处理复杂。多相流计量一般是分别获得其中一相或各相的瞬时或累积流量。在一般的多相流中，各相的流速不相等，而且随各相的物性、流动状况而产生不同的流速模型，在含有粉粒的固液、固气两相流中，粒度分布、粒径、浓度等对流速有很大的影响。所以，目前还没有确定从其流动状况来控制流量的一般方法，而摇根据实际情况，选用最合适的测量方法。 (王池)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条