1) reduction-coprecipitation
还原-化学共沉淀法
2) co-precipitation-decomposition
化学共沉淀-共还原
1.
This paper introduces the method of preparation of catalyst powder FeNi27Co3 by the way of co-precipitation-decomposition,and studies the influence of pH value,metal ion concentration,feed rate and the amount of additives on sediment formation and particle size.
介绍了利用化学共沉淀-共还原方法制备FeNi27Co3触媒粉的过程,研究了pH值、金属离子浓度、加料速度、添加剂用量对沉淀物产生和粒度的影响,确定出工艺条件为:溶液pH值为3左右,沉淀物450℃煅烧3h,然后再通过650℃氢气还原3h;并得到了D50约为9μm,氧含量为0。
3) redox coprecipitation
氧化还原共沉淀法
1.
MnOx-SnO2 composite oxides prepared by a redox coprecipitation route were tested in selective catalytic reduction of NO by NH3 at low temperature.
采用氧化还原共沉淀法制备了MnOx-SnO2复合氧化物,并将其用于低温NH3选择催化还原NO反应。
4) co-precipitation and reduction
共沉淀还原法
1.
Copper base prealloyed powder for diamond tools matrix was prepared by co-precipitation and reduction method.
采用共沉淀还原法制取金刚石制品胎体的铜基预合金粉末。
5) Precipitation-reduction method
沉淀共还原法
6) reductive co-precipitation method
共还原沉淀法
1.
Nano-sized Cu-Sn alloy powders were prepared by reductive co-precipitation method combined with aging treatment in constant temperature water bath at 80 ℃.
采用共还原沉淀法制得Cu-Sn合金负极材料Cu6Sn5和Cu6Sn4,并分别进行不同时间的时效处理,对所得样品进行XRD分析、场发射SEM图像观察和恒流充放电性能测试。
补充资料：化学共沉淀法
分子式：
CAS号：
性质：将适当的原料按化学式计量配比溶于一定的溶剂中配成含有一定浓度的多种可溶性阳离子的盐溶液，然后加入适当沉淀剂(如OH-，CO-，C2O42-等)，控制一定pH值，使各种阳离子同时形成不溶性氢氧化物、碳酸盐或草酸盐的沉积物。对沉淀物经后处理而得到所需的粉体的一种方法。沉积剂的种类和用量的适当选择是确保共沉淀完全的关键。另外，溶液的浓度、pH值、温度等对共沉淀过程有相当的影响。化学共沉淀法工艺简便，制得粉体性能良好，已广泛应用于多种陶瓷粉体的制备。如ZrO2(Y2O3)等的氧化物陶瓷粉体。选用ZrOCl2·8H2O和YCl3为原料，用NH4OH为沉淀剂，控制适当的共沉淀条件并经一定的后处理可获得颗粒为亚微米级，且具有良好烧结性能的ZrO2(Y2O3)粉体。
CAS号：
性质：将适当的原料按化学式计量配比溶于一定的溶剂中配成含有一定浓度的多种可溶性阳离子的盐溶液，然后加入适当沉淀剂(如OH-，CO-，C2O42-等)，控制一定pH值，使各种阳离子同时形成不溶性氢氧化物、碳酸盐或草酸盐的沉积物。对沉淀物经后处理而得到所需的粉体的一种方法。沉积剂的种类和用量的适当选择是确保共沉淀完全的关键。另外，溶液的浓度、pH值、温度等对共沉淀过程有相当的影响。化学共沉淀法工艺简便，制得粉体性能良好，已广泛应用于多种陶瓷粉体的制备。如ZrO2(Y2O3)等的氧化物陶瓷粉体。选用ZrOCl2·8H2O和YCl3为原料，用NH4OH为沉淀剂，控制适当的共沉淀条件并经一定的后处理可获得颗粒为亚微米级，且具有良好烧结性能的ZrO2(Y2O3)粉体。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。