1) Light weight castables
轻质浇注料
1.
Light weight castables were prepared using glazed hollow microsphere (addition from 40% to 60%) with low bulk density,low water absorption rate and low thermal conductivity and CA-70 high alumina cement (addition from 40% to 60%).
以体积密度小、吸水率低、热导率低的玻化微珠(加入量为40%~60%)和CA-70高铝水泥(加入量为40%~60%)为原料研制了轻质浇注料,并分别研究了玻化微珠用量对轻质浇注料常温强度、体积密度、烧后线变化率的影响。
2) light castables
轻质耐火浇注料
1.
Based on the components and properties of the domestic light castables and the flue actual working conditions of furnace to producegas, the improving technology demands of the light castables of expanding pearl rock were put forward for the actual problems of flue liner.
根据国内轻质耐火浇注料的组成与性能以及煤气发生炉烟道的实际工作条件,针对烟道内衬实际存在的问题,提出了内衬膨胀珍珠岩轻质耐火浇注料的改进技术要求,并确定了在保证膨胀珍珠岩浇注料保温隔热性能的前提下,提高浇注料的力学性能、抗热震性能和防爆性能的研究内容。
3) High Alumina Lightweight Castable
高铝质轻质浇注料
4) light air hardening pouring material
气硬性轻质浇注料
1.
According to design, the lining with light air hardening pouring material was needed to lay onto convection chamber, chimney and the bottom of heater of catalytic reformed equipment.
某石化总厂催化重整装置,设计要求其中的加热炉对流室、烟囱和炉底均采用气硬性轻质浇注料进行衬里,为此对气硬性轻质浇注料进行了研制。
5) high strength light pourable refractory
高强度轻质耐火浇注料
6) light mullite refractory castables
莫来石轻质耐火浇注料
补充资料：轻质硅酸盐集料
分子式：
CAS号：
性质：一种不能水溶的硅酸盐膨胀集料。典型成分为无水硅酸钠，其中氧化钠比二氧化硅为1:2.36。另加入氧化钡，使用时向集料中加入固化剂（硼酸、氯化硼或硼酸钠），再加入水即发生水合作用并固化。碾碎后快速加热到510～540℃使其膨胀。密度为20.8～27.2kg/m3。为优良的轻质制品。
CAS号：
性质：一种不能水溶的硅酸盐膨胀集料。典型成分为无水硅酸钠，其中氧化钠比二氧化硅为1:2.36。另加入氧化钡，使用时向集料中加入固化剂（硼酸、氯化硼或硼酸钠），再加入水即发生水合作用并固化。碾碎后快速加热到510～540℃使其膨胀。密度为20.8～27.2kg/m3。为优良的轻质制品。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条