1) curing temperature field
硫化温度场
1.
Influence of curing reaction heat on curing temperature field of rubber;
橡胶硫化反应热对硫化温度场的影响
2.
A model was built by using ANSYS to simulate the curing temperature field of two green tires,of which one was preheated and another was not.
采用ANSYS建立轮胎硫化温度场分析模型 ,对经过预热和未经预热处理两种情况下的胎坯硫化温度场进行了模拟。
2) curing temperature
硫化温度
1.
The curing temperature of9 00-2016PR tire in autoclave was determined withJLW 12 Curing Temperature Tester.
００－２０１６ＰＲ轮胎进行硫化温度测定，获得了硫化温度在轮胎各部位的变化情况，并以此得到各部位胶料的硫化程度，发现均存在过硫现象，适当调整工艺条件，硫化外温由１４３℃改为１５１℃，硫化时间缩短５ｍｉｎ后，轮胎机床耐久性能提高显著。
2.
Study on property and curing temperature of low elasticity shock-absorbing blowing material;
较好的硫化温度为433～443K,最佳温度为438K。
4) State of curing field
硫化程度场
5) temperature variation field
变化温度场
1.
Based on the research achievement of Document [2] and [3], a method is presented for calculating the temperature variation field of arch dam with insulation layer.
为了降低温度荷载,在拱坝下游面粘贴聚苯乙烯塑料板作为永久保温层,在文献[2]、[3]研究基础上,提出了有保温层拱坝变化温度场的计算方法。
6) homogenizing of temperature field
温度场均化
补充资料：硫化温度
分子式：
CAS号：
性质：指橡胶加热硫化时的温度。胶料硫化时所需的温度取决于生胶种类、硫化体系和产品结构等因素。天然橡胶胶料的硫化温度不宜高于150～160℃，各种合成橡胶的适宜硫化温度一般为150～160℃。其中丁基橡胶及乙丙橡胶硫化宜在170℃左右。硫化反应速度随温度的升高而加快，一般是温度每升高10℃，硫化反应速度约加快一倍，即硫化时间相对约减少一半。橡胶制品的实际硫化温度是根据胶料配方、产品结构与体积、硫化设备、内部补强织物等因素，经实验而确定的。
CAS号：
性质：指橡胶加热硫化时的温度。胶料硫化时所需的温度取决于生胶种类、硫化体系和产品结构等因素。天然橡胶胶料的硫化温度不宜高于150～160℃，各种合成橡胶的适宜硫化温度一般为150～160℃。其中丁基橡胶及乙丙橡胶硫化宜在170℃左右。硫化反应速度随温度的升高而加快，一般是温度每升高10℃，硫化反应速度约加快一倍，即硫化时间相对约减少一半。橡胶制品的实际硫化温度是根据胶料配方、产品结构与体积、硫化设备、内部补强织物等因素，经实验而确定的。