1) vacuum assisted resin transfer molding
真空辅助树脂传递模塑
1.
This paper outlineed traditional resin transfer molding and a series of new-type RTM technology,such as vacuum assisted resin transfer molding,Seemann composite resin infusion molding,resin film infusion,and introduced their manufacturing process,typical advantages,their present limitations and solution.
概述了传统树脂传递模塑(RTM)及在其基础上发展起来的新型RTM工艺,包括真空辅助树脂传递模塑(VARTM)、Seemann复合材料树脂浸渍模塑成型工艺(SCRIMP)和树脂膜渗透成型工艺(RFI)的成型原理、优点,并指出目前存在的缺点及解决方法。
2) VARTM
真空辅助树脂传递模塑
1.
The rheological behavior of epoxy resin for vacuum assisted resin transfer molding(VARTM) was studied with DSC analysis and viscosity experiments.
研究了真空辅助树脂传递模塑(VARTM)工艺用环氧树脂(EP)体系的流变特性,结合差示扫描量热(DSC)仪和旋转式粘度计对A1、A2、A3三种EP体系的测试结果,确定A2树脂体系适合于VARTM工艺,并根据双阿累尼乌斯方程,建立了A2树脂体系的流变模型。
3) vacuum assisted resin transfer molding(VARTM)
真空辅助树脂传递模塑(VARTM)
4) Vacuum-Assisted Resin Transfer Molding (VARTM)
真空辅助树脂传递注塑(VARTM)
6) RTM
树脂传递模塑
1.
Through applying a liquid modified aromatic amine as curing agent for epoxy resin,a high performance resin matrix system for resin transfer moulding(RTM) was derived.
选用一种液体改性芳香胺为环氧树脂的固化剂,得到了一种适合于树脂传递模塑(RTM)的高性能树脂体系。
2.
5D braided quartz/phenolic composites were made by advanced RTM.
5D石英 /酚醛复合材料作了初步的研究 ,采用先进的树脂传递模塑(RTM)工艺进行复合成型 ,并对其力学性能、热物理性能和烧蚀性能做了研究与分析。
补充资料：传递模塑
制造热固性塑料制品常用的塑料加工方法，也用于橡胶加工。热固性塑料或橡胶料（可以先行预热）在加料室内加热、熔融（图a）,再在加压下进入加热的闭合型腔内（图b）,经过固化后（或硫化），脱模即得制品。
传递模塑与模压相仿，都借助于压机，但又有注射成型的特点，模具设有浇口和流道。
这种方法要求热固性塑料，在未达到固化温度以前具有较大的流动性，而达到固化温度后又具有较快的固化速率，如酚醛树脂、三聚氰胺－甲醛树脂和环氧树脂等。用于橡胶制品加工时，胶料必须流动性好，硫化快。此法与模压相比，其优点是固化较均匀,生产周期短,尺寸精确度好，飞边修饰较易，嵌件和芯子不易变形，特别适于生产镶嵌件的制品。缺点是模具费用较大，模腔、浇口、流道中剩余料无法回收，故原材料单耗稍高。
传递模塑与模压相仿，都借助于压机，但又有注射成型的特点，模具设有浇口和流道。
这种方法要求热固性塑料，在未达到固化温度以前具有较大的流动性，而达到固化温度后又具有较快的固化速率，如酚醛树脂、三聚氰胺－甲醛树脂和环氧树脂等。用于橡胶制品加工时，胶料必须流动性好，硫化快。此法与模压相比，其优点是固化较均匀,生产周期短,尺寸精确度好，飞边修饰较易，嵌件和芯子不易变形，特别适于生产镶嵌件的制品。缺点是模具费用较大，模腔、浇口、流道中剩余料无法回收，故原材料单耗稍高。