1) alkali-activated carbonatite-slag grouting material
碱碳酸盐矿-矿渣灌浆材料
1.
The effect of some setting retarders on the workability of alkali-activated carbonatite-slag grouting material(AACSGM for short) was investigated.
研究了数种缓凝剂对碱碳酸盐矿-矿渣灌浆材料工作性能的影响。
2) alkali activated carbonatites-slag grouting material
碱激发碳酸盐矿-矿渣复合灌浆材料
1.
It was studied that by using the Marsh cone flow time of subsection to substitute the rheometer to test the rheological behaviour of alkali activated carbonatites-slag grouting material pastes,and the corresponding relation of the test results of the Marsh cone flow time of subsection and the rheometer was discussed by computing of simple model.
探讨了采用简单分段Marsh时间替代流变仪测试碱激发碳酸盐矿-矿渣复合灌浆材料浆液流变性能的方法,并把分段Marsh时间测试结果通过简单的模型计算,寻找它与流变仪测定的流变性能结果之间的对应关系。
2.
The simulated grouting experiment of alkali activated carbonatites-slag grouting material (AACSGM) pastes was carried out in laboratory, and grouting process parameters under laboratory conditions are obtained as follows: the grouting pressure being 2.
通过对碱激发碳酸盐矿-矿渣复合灌浆材料进行实验室模拟灌浆试验研究,获得实验室条件下灌浆工艺参数是:灌浆压力2。
3) alkali activated-carbonatites-slag grouting material
碱激发碳酸盐-矿渣复合灌浆材料
1.
The workability of alkali activated-carbonatites-slag grouting materials with different proportioning was studied,in which Marsh cone flow time and mini-slump in combination with conventional gelation time test were adopted to characterize the apparent viscosity and yield stress of the materials.
在碱激发碳酸盐-矿渣复合灌浆材料试验研究中引入浆液Marsh时间与Mini扩展度试验方法,以表征浆液的表观粘度和屈服应力,并结合传统的凝胶时间试验方法,综合研究了不同配方浆液的工作性能。
4) Alkali-activated-carbonatite cementitious material for grouting
碱激发碳酸盐胶凝-灌浆材料
5) alkali-slag cementitious material
碱-矿渣胶凝材料
6) alkali-slag cementation materials
碱矿渣胶凝材料
1.
Application of alkali-slag cementation materials in rapid determination of fired perforated bricks compressive strength
碱矿渣胶凝材料在快速测定烧结多孔砖抗压强度中的应用
补充资料：灌浆材料
| 灌浆材料 grout 在压力作用下注入地层、岩石或构筑物的缝隙、孔洞中，达到增加承载能力、防止渗漏及提高构筑物整体性能等效果的流体材料。分固体灌浆材料和化学灌浆材料两大类。固体灌浆材料是由固体颗粒和水组成的悬浮液，有粘土浆、水泥浆、水泥粘土浆、水泥粉煤灰浆4种。它取材方便，造价低，施工简单，有较好的防渗或固结能力，但所填缝隙宽度受固体颗粒细度的限制。掺用塑化剂、促凝剂可改善固体灌浆材料的性能。化学灌浆材料是由化学药剂制成的流动性好的液体，能灌入比较细微的缝隙，还能根据需要调节凝结时间，常用的有：①硅化用灌浆材料。以硅酸钠(水玻璃)为主要原料的化学浆液，用于砂质土、黄土的加固和防渗。②环氧树脂灌浆材料。以环氧树脂为主，加入一定比例的固化剂、稀释剂、增韧剂混合而成，用于结构混凝土的补强和裂缝堵漏。③甲凝。以甲基丙烯酸甲酯、甲基丙烯酸丁酯为主要原料，加入过氧化苯甲酰、二甲基苯胺和对甲苯亚磺酸组成的一种低粘度灌浆材料，用于大坝、油管、船坞和基础等混凝土的补强和堵漏。④丙凝。以丙烯酰胺为基料，以甲醛、过硫酸胺、三乙醇胺、硫酸亚铁、铁氰化钾为助剂，将氧化材料和其他材料分别配制成两种溶液，按一定比例同时灌注，主要用于防渗堵漏工程。⑤氰凝。由异氰酸酯、聚醚和促进剂配制而成，用于地下工程的渗漏缝处理。 |