1) poly(amide-sulfone)
聚芳砜酰胺
1.
A series of poly(amide-sulfone) with different intrinsic viscosity were synthesized via 4,4′-DDS,3,3′-DDS and TPC at low temperature.
以4,4′-二氨基二苯基砜(4,4-′DDS),3,3′-二氨基二苯基砜(3,3-′DDS),对苯二甲酰氯(TPC)为单体,通过低温溶液缩聚反应合成了一系列聚芳砜酰胺三元共聚物。
2) polyarylene sulfide sulfone amide
聚芳硫醚砜酰胺
1.
Diamine monomer containing sulfide was synthesized firstly,then polyarylene sulfide sulfone amide(PASSA)with high molecular weight was synthesized at low temperature.
与以往的以硫化钠为硫源采用高温聚合合成聚芳硫醚类树脂的方法不同,采用先合成含硫醚键的单体,然后进行低温溶液缩聚,合成了高分子量的新型聚芳硫醚砜酰胺(PASSA)树脂,其特性粘度可达到0。
2.
Diamine monomers containing sulfone or ketone group were synthesized firstly,then polyarylene sulfide sulfone amide(PASSA) and polyarylene sulfide ketone amide(PASKA) with high molecular weight were synthesized by a low temperature polycondensation reaction in anhydrous N-methylpyrrolidone (NMP).
采用先合成含硫醚键的单体,后进行低温溶液缩聚的方法,合成高分子量的新型聚芳硫醚酰胺类树脂——聚芳硫醚砜酰胺(PASSA)和聚芳硫醚酮酰胺(PASKA),其特性粘数分别为0。
3) aromatic polysulphonamide fiber
聚芳砜酰胺纤维
4) poly(aryl oxide sulfone-imide)
聚芳醚砜酰亚胺
5) polyarylene sulfide sulfone imide
聚芳硫醚砜酰亚胺
1.
A novel heat-resistant material polyarylene sulfide sulfone imide (PASSI) was synthesized successfully.
用化学酰亚胺技术首先合成含完全酰亚胺环的单体,然后与Na2S常压聚合,从而在聚芳硫醚分子主链中引入了刚性的酰亚胺环,合成聚芳硫醚砜酰亚胺(PASSI),并对单体及聚合物进行表征,通过热分析得出聚合物的玻璃化温度为252。
6) chloride-polysulfonamide
芳香含氯聚砜酰胺
1.
The effect of the technology of thermal stretching on chloride-polysulfonamide (Cl-PSA) fiber spun by wet methods is studied in this paper.
观察芳香含氯聚砜酰胺纤维结构性能对拉伸倍率和温度的依赖性。
补充资料：聚芳砜
聚芳砜是由4，4’-二磺酞氯二苯醚与联苯反应制得。琥珀色透明颗粒。相对密度(25℃／4℃)1.371，折射率1．652，耐热性比双酚A型聚砜高得多，热变形温度和连续使用温度均高100℃左右。玻璃化温度288℃，连续使用温度260℃，热变形温度274℃(1.82MPa)。耐酸、碱、乙醇、丙酮、醋酸乙酯、烃类、燃料油、润滑油等。溶于二甲基甲酰胺、二甲基乙酰胺、N-甲基-2-吡咯烷酮、二甲基亚砜、四甲基亚砜等。吸水性大(3．1％)，熔融粘度高。
相对密度 1.36
拉伸强度 89MPa
弯曲强度 118MPa
伸长率 13％
洛氏硬度 M110
相对密度 1.36
拉伸强度 89MPa
弯曲强度 118MPa
伸长率 13％
洛氏硬度 M110