1) longitudinal corner crack
角部纵裂
1.
Due to frequent emergencies of bleeding out by the billet longitudinal corner crack,the characteristic and mechanism of bleeding out are analyzed.
由于方坯角部纵裂漏钢事故频繁,通过分析漏钢的特点和机理,认为造成小方坯角部纵裂漏钢的主要原因是结晶器倒锥度小、结晶器液面波动及中间包过热度大、结晶器冷却水质差。
2.
1 steelmaking plant of WISCO in 2006 have been made and the main characteristics and mechanism of sticking breakout and longitudinal corner crack induced breakout analyzed.
统计了武钢一炼钢厂方坯连铸机2006年的漏钢情况,分析了粘结漏钢和角部纵裂漏钢的特点及机理,并找出了产生粘结漏钢和角部纵裂漏钢的主要原因是保护渣的性能、结晶器的精度、钢水的过热度、拉速及浸入式水口的对中等。
2) the breakout of longitudinal cracks in corner
角部纵裂漏钢
3) longitudinal crack at deflec-tion angle
偏离角纵裂
4) the axial longitudinal faults
轴部纵断裂
5) longitudinal edge crack
边部纵裂纹
1.
Cause and solution to longitudinal edge crack in slab;
板坯边部纵裂纹产生的原因及解决措施
6) transverse corner crack
角部横裂
1.
Causes and countermeasures of transverse corner crack on narrow continuous casting slab;
连铸窄板坯角部横裂的成因及对策
补充资料：纵裂