1) polycarbonate urethane
聚碳酸酯聚氨酯
1.
Structure and performance of polycarbonate urethane;
聚碳酸酯聚氨酯的结构及性能
2.
Construction and characterization of a novel sulfoammonium zwitterionic structure onto surface of polycarbonate urethane film;
聚碳酸酯聚氨酯膜表面构建新型磺铵两性结构及其表征
3.
In order to improve the blood-compatibility of polycarbonate urethane (PCU), the surface of PCU film was forced to generate and release endogenous NO via blending with Cu(II)-complex and grafting endogenous NO donors.
为了提高聚碳酸酯聚氨酯(PCU)的血液相容性,本文通过共混和接枝的方法,使聚碳酸酯聚氨酯膜表面能释放内源性NO,以此来提高材料的抗凝血性。
2) polycarbonate-polyurethane
聚碳酸酯聚氨酯
1.
In order to study the structure and properties of polycarbonate-polyurethane (PCU), it was synthesized by two different methods and followed by surface modification.
为了研究聚碳酸酯聚氨酯的结构与性能,本文用两种方法合成了聚碳酸酯聚氨酯,对其进行了表面改性,并用多种方法进行表征。
3) polycarbonate urethanes
聚碳酸酯聚氨酯
1.
In the present work, three kinds of polycarbonate urethanes (PCUs) having 40%(mass%) MDI/BDO hard segments were synthesized from poly (tetramethylene carbonate) diol(PBC), poly(hexamethylene carbonate) diol(PHC) and poly(hexamethylene-co-pentamethylene carbonate) diol (PHPC,the molar ratio of hexamethylene and pentamethylene units are 3∶2),respectively, by bulk one-shot method.
采用了聚碳酸 1,4 -丁二醇酯 ( PBC)、聚碳酸 1,6-己二醇酯 ( PHC)和聚碳酸 1,5 -戊二醇 - 1,6-己二醇酯 ( PHPC,其中己二醇链节与戊二醇链节之比为 3∶ 2 )软段 ,4 ,4′-二苯基甲烷二异氰酸酯 / 1,4 -丁二醇 ( MDI/ BDO)为硬段 (其质量含量为 4 0 % )合成出了一系列的聚碳酸酯聚氨酯 ( PCU)弹性体。
4) polycarbonate polyurethane
聚碳酸酯型聚氨酯
1.
A series of polycarbonate polyurethane(PCU) were prepared with poly(hexamethylene carbonate) diol as soft segment,trimethylol propane and isophorone diisocyanatet as hard segment.
采用溶液预聚法合成了以聚1,6-己二醇碳酸酯二醇(PHMCD)为软段、异佛尔酮二异氰酸酯(IPDI)和三羟甲基丙烷(TMP)为硬段的聚碳酸酯型聚氨酯(PCU),研究了原料配比对PCU性能的影响,利用红外光谱(FT-IR)等对PCU的结构进行了表征,测试了其力学性能和形状记忆性能。
2.
The developmental trends of polycarbonate diols and polycarbonate polyurethane was summarized.
本文论述了聚碳酸酯二元醇及聚碳酸酯型聚氨酯材料的发展概况 ,并分别简述了聚碳酸酯二元醇的合成方法、应用及聚碳酸酯型聚氨酯材料的性能与特
3.
A series of linear polycarbonate polyurethanes (PCUs) with variation of NCO/OH molar ratio and hard segment content was synthesized by solution two-step polymerization, using dibutyltin dilaurate (DBTDL) as catalyst.
随着现代医学的发展,新的医学材料的出现,对生物材料要求越来越高,而聚碳酸酯型聚氨酯材料正是这样一种对生物稳定性、对人体安全很有应用前景的植入材料。
5) Polyi-midocarbonate
聚亚氨碳酸酯
补充资料：聚对苯二甲酸丁二酯/聚碳酸酯共混物
分子式：
CAS号：
性质： PC与PBT都是聚酯类聚合物，机械共混时必须把原料充分干燥且避免温度过高以及在受热状态下停留时间过长，否则将因发生酯交换反应导致共混物性能劣化。另外的对策是加入各种稳定剂以阻止酯交换反应的发生。当PC含量很少时体系是部分相容的，PC占30％～40％时则完全相容，若PC含量比较多而又少于30％时，PBT/PC共混体系成为PBT；PC、PBT/PC相容物的共混体系。PBT中加入PC对冲击强度的提高尚不很突出，若同时加人橡胶类物质，则增韧效果更好。PC的加入使得PBT结晶度下降，对PBT因结晶引起制品易翘曲变形的特点得以改善，这种效果对于玻璃纤维增强PBT尤其重要。
CAS号：
性质： PC与PBT都是聚酯类聚合物，机械共混时必须把原料充分干燥且避免温度过高以及在受热状态下停留时间过长，否则将因发生酯交换反应导致共混物性能劣化。另外的对策是加入各种稳定剂以阻止酯交换反应的发生。当PC含量很少时体系是部分相容的，PC占30％～40％时则完全相容，若PC含量比较多而又少于30％时，PBT/PC共混体系成为PBT；PC、PBT/PC相容物的共混体系。PBT中加入PC对冲击强度的提高尚不很突出，若同时加人橡胶类物质，则增韧效果更好。PC的加入使得PBT结晶度下降，对PBT因结晶引起制品易翘曲变形的特点得以改善，这种效果对于玻璃纤维增强PBT尤其重要。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。